1、Designation:C836/C836M15Standard Specification forHigh Solids Content,Cold Liquid-Applied ElastomericWaterproofing Membrane for Use with Separate WearingCourse1This standard is issued under the fixed designation C836/C836M;the number immediately following the designation indicates the yearof origina
2、l adoption or,in the case of revision,the year of last revision.A number in parentheses indicates the year of last reapproval.A superscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This specification describes the required properties andtest methods for
3、 a cold liquid-applied elastomeric-typemembrane,one-or two-component,for waterproofing buildingdecks and walls subject to hydrostatic pressure in buildingareas to be occupied by personnel,vehicles,or equipment.Thisspecification applies only to a membrane system that will becovered with a separate we
4、aring course,traffic course,orbackfill.NOTE1See Guide C898 and Guide C1471 for proper application ofmembrane.1.2 There are no ISO standards similar or equivalent to thisASTM standard.1.3 The values stated in either SI units or inch-pound unitsare to be regarded separately as standard.The values stat
5、ed ineach system may not be exact equivalents;therefore,eachsystem shall be used independently of the other.Combiningvalues from the two systems may result in non-conformancewith the standard.1.4 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is
6、 theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2.Referenced Documents2.1 ASTM Standards:2C794 Test Method forAdhesion-in-Peel of Elastomeric JointSealantsC898 Guide for Use
7、of High Solids Content,Cold Liquid-Applied Elastomeric Waterproofing Membrane with Sepa-rate Wearing CourseC1305 Test Method for Crack Bridging Ability of Liquid-Applied Waterproofing MembraneC1375 Guide for Substrates Used in Testing Building Sealsand SealantsC1471 Guide for the Use of High Solids
8、Content ColdLiquid-Applied Elastomeric Waterproofing Membrane onVertical SurfacesC1522 Test Method for Extensibility After Heat Aging ofCold Liquid-Applied Elastomeric Waterproofing Mem-branesD1079 Terminology Relating to Roofing and WaterproofingD2240 Test Method for Rubber PropertyDurometer Hard-n
9、essD6511 Test Methods for Solvent Bearing Bituminous Com-pounds3.Terminology3.1 DefinitionsRefer to Terminology D1079 for defini-tions of the terms used in this specification.4.Classification4.1 Types:4.1.1 Type IA one-component,cold liquid-applied water-proofing material suitable for immediate appl
10、ication aftermixing.Type I products may be used with an accelerator thatis beneficial but not essential for curing of the membrane.4.1.2 Type IIAtwo-component,cold liquid-applied water-proofing material.Combining two components is essential forcuring of the membrane.5.Physical Requirements5.1 Materi
11、alMembrane materials shall cure,after appli-cation by spreading or spraying,to form an elastomeric filmcapable of maintaining a seal against liquid water.5.2 The physical,mechanical,and performance propertiesof the membrane shall conform to the requirements describedin Table 1.1This specification is
12、 under the jurisdiction of ASTM Committee D08 onRoofing and Waterproofing and is the direct responsibility of Subcommittee D08.22on Waterproofing and Dampproofing Systems.Current edition approved June 1,2015.Published June 2015.Originallyapproved in 1976.Last previous edition approved in 2012 as C83
13、6/C836M 12.DOI:10.1520/C0836_C0836M-15.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.Copyright ASTM Internationa
14、l,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United States1 6.Test Methods6.1 Standard ConditionsStandard conditions for all testsshall be 23 6 2C 73.4 6 3.6F and 50 6 5%relativehumidity.6.2 Conditioning/Mixing:6.2.1 Store all membrane materials to be tested in anunopened cont
15、ainer at standard conditions for at least 24 hbefore any test specimens are prepared.6.2.2 Follow the manufacturers instructions for mixing andpreparing membrane materials for testing.Thoroughly mixone-component samples before using.Mix two-componentcompounds in the ratio recommended by the manufact
16、urer.6.3 Test SurfacesIn addition to the mortar test surfacesspecified,use other test surfaces when required by the specifier.6.4 PrimerWhen required by the manufacturer,use aprimer as directed by the manufacturer on all substrate mate-rials in test assemblies.6.5 Hardness:6.5.1 Following the manufacturers instructions,apply afilm of membrane,1.5 6 0.1 mm 60 6 5 mils thick,on a 100by 150-mm 4 by 6-in.piece of polyethylene film-coatedpaper and allow the membrane to cure for 14 days at standardcon