1、Designation:A968/A968M96(Reapproved 2014)Standard Specification forChromium,Chromium-Nickel,and Silicon Alloy Steel Barsand Shapes for Corrosion and Heat-Resisting Service1This standard is issued under the fixed designation A968/A968M;the number immediately following the designation indicates the ye
2、arof original adoption or,in the case of revision,the year of last revision.A number in parentheses indicates the year of last reapproval.A superscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This specification covers hot-and cold-finished alloysteel b
3、ars having a chromium content equal to or less than11.0%including rounds,squares,hexagons,and hot-rolled orextruded shapes for use in corrosion and heat-resisting service.1.2 Some steels covered by this specification,especially thehigh silicon-containing steels,because of their particular alloyconte
4、nt and specialized properties,may require special care intheir fabrication and welding.Specific procedures are offundamental importance,and it is presupposed that all param-eters will be in accordance with approved test methods capableof producing the desired properties in the finished fabrication.1
5、.3 The values stated in either SI units or inch-pound unitsare to be regarded separately as standard.The values stated ineach system may not be exact equivalents;therefore,eachsystem shall be used independently of the other.Combiningvalues from the two systems may result in non-conformancewith the s
6、tandard.1.4 This specification and the applicable material specifica-tions are expressed in both inch-pound and SI units.However,unless the order specifies the applicable“M”specificationdesignation(SI units),the material shall be furnished ininch-pound units.2.Referenced Documents2.1 ASTM Standards:
7、2A484/A484M Specification for General Requirements forStainless Steel Bars,Billets,and ForgingsA751 Test Methods,Practices,and Terminology for Chemi-cal Analysis of Steel ProductsE527 Practice for Numbering Metals and Alloys in theUnified Numbering System(UNS)2.2 SAE Standard:SAE J 1086 Recommended
8、Practice for Numbering Metalsand Alloys33.Ordering Information3.1 It is the responsibility of the purchaser to specify allrequirements that are necessary for material ordered under thisspecification.Such requirements may include,but are notlimited to,the following:3.1.1 Quantity(weight or number of
9、pieces);3.1.2 Dimensions,including diameter or thickness(andwidth),shape or form,applicable prints or sketches,length,andso forth;3.1.3 Type or UNS designation(see Table 1);3.1.4 ASTM designation and edition year if other than latestedition;3.1.5 Heat-treated condition(see Section 5);3.1.6 Finish(se
10、e Manufacture section of SpecificationA484/A484M);3.1.7 Supplementary requirements invoked for special ser-vices;3.1.8 Whether bars are to be rolled as bars or cut from stripor plate;3.1.9 Preparation for delivery(see Preparation for Deliverysection of Specification A484/A484M);3.1.10 Marking requir
11、ements(see Marking section ofSpecification A484/A484M);3.1.11 Surface preparation of shapes(see Manufacture sec-tion of Specification A484/A484M);and3.1.12 The intended use of the material,if the purchaserconsiders this useful information.NOTE1A typical ordering description is as follows:5000 lb 200
12、0kg;1.000-in.25-mm round bar by 10 to 12 ft 3 to 4 m;UNS S70003;to Specification A XXX A XXX;annealed;centerless ground;plus anyoptional supplementary requirements;such as,for example,specialmarking instructions.4.General Requirements4.1 In addition to the requirements of this specification,allrequi
13、rements of the current editions of Specification A484/1This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys and is the direct responsibility of SubcommitteeA01.17 on Flat-Rolled and Wrought Stainless Steel.Current edition approved March 1,201
14、4.Published April 2014.Originallyapproved in 1996.Last previous edition approved in 2009 as A968/A968M-96(2009).DOI:10.1520/A0968_A0968M-96R14.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume
15、 information,refer to the standards Document Summary page onthe ASTM website.3Available from Society of Automotive Engineers,400 Commonwealth Drive,Warrendale,PA 15096.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United States1Copyright by ASTM Intl(
16、all rights reserved);A484Mshall apply.Failure to comply with the general requirements of Specifi-cation A484/A484M constitutes nonconformance with this specification.5.Heat Treatment5.1 UNS S70003 shall be furnished in the solution annealedcondition with subsequent light drawing and straighteningpermitted.6.Chemical Composition6.1 Chemical composition shall be reported to thepurchaser,or his representative,and shall conform to therequirements specified in Table 1.6.2 When a product analysis is p