1、Designation:B352/B352M17Standard Specification forZirconium and Zirconium Alloy Sheet,Strip,and Plate forNuclear Application1This standard is issued under the fixed designation B352/B352M;the number immediately following the designation indicates the yearof original adoption or,in the case of revisi
2、on,the year of last revision.A number in parentheses indicates the year of last reapproval.A superscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This specification covers hot-and cold-rolled zirconiumand zirconium alloy sheet,strip,and plate.1.2 One un
3、alloyed and three alloys for use in nuclearapplications are described.1.3 The products covered in this specification include thefollowing forms and sizes:1.3.1 Sheet,24 in.600 mm or more in width;under 0.187in.4.8 mm)in thickness,1.3.2 Strip,less than 24 in.600 mm in width;under 0.187in.4.8 mm in th
4、ickness,and1.3.3 Plate,over 10 in.250 mm in width;0.187 in.4.8mm and over in thickness.NOTE1Material over 0.187 in.4.8 mm in thickness and less than 10in.250 mm wide is covered as bar in Specification B351/B351M.1.4 Unless a single unit is used,for example corrosion massgain in mg/dm2,the values sta
5、ted in either inch-pound or SIunits are to be regarded separately as standard.The valuesstated in each system are not exact equivalents;therefore eachsystem must be used independently of the other.SI valuescannot be mixed with inch-pound values.1.5 The following precautionary caveat pertains only to
6、 thetest method portions of this specification.This standard doesnot purport to address all of the safety concerns,if any,associated with its use.It is the responsibility of the user of thisstandard to establish appropriate safety and health practicesand determine the applicability of regulatory lim
7、itations priorto use.1.6 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations issued by the World Trade Organization
8、TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2B350/B350M Specification for Zirconium and ZirconiumAlloy Ingots for Nuclear ApplicationB351/B351M Specification for Hot-Rolled and Cold-Finished Zirconium and Zirconium Alloy Bars,Rod,andWire for Nuclear ApplicationE
9、8/E8M Test Methods for Tension Testing of Metallic Ma-terialsE21 Test Methods for Elevated Temperature Tension Tests ofMetallic MaterialsE29 Practice for Using Significant Digits in Test Data toDetermine Conformance with SpecificationsE114 Practice for Ultrasonic Pulse-Echo Straight-BeamContact Test
10、ingE1001 Practice for Detection and Evaluation of Discontinui-ties by the Immersed Pulse-Echo Ultrasonic MethodUsing Longitudinal WavesG2/G2M Test Method for Corrosion Testing of Products ofZirconium,Hafnium,and Their Alloys in Water at 680F(360C)or in Steam at 750F(400C)3.Terminology3.1 Definitions
11、 of Terms Specific to This Standard:3.1.1 annealed,ndenotes material that exhibits a recrys-tallized grain structure.3.2 Lot Definition:3.2.1 Sheet,strip,and plate products(single definition,common to nuclear and non-nuclear standards),na lot shallconsist of a material of the same size,shape,conditi
12、on,andfinish produced from the same ingot or powder blend by thesame reduction schedule and the same heat treatment param-eters.Unless otherwise agreed between manufacturer andpurchaser,a lot shall be limited to the product of an 8 h periodfor final continuous anneal,or to a single furnace load for
13、finalbatch anneal.1This specification is under the jurisdiction of ASTM B10 on Reactive andRefractory Metals and Alloys and is the direct responsibility of B10.02 onZirconium and Hafnium.Current edition approved May 1,2017.Published May 2017.Originallyapproved in 1960.Last previous edition approved
14、in 2016 as B352/B352M 11(2016).DOI:10.1520/B0352_B0352M-17.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.Copyrig
15、ht ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Sta
16、ndards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.1 4.Ordering Information4.1 Purchase orders for material under this specificationshould include the following information as required to ad-equately describe the desired material:4.1.1 Quantity(weight or number of pieces),4.1.2 Name of material,4.1.3 Condition(Section 6),4.1.4 Finish(Section 14),4.1.5 Form(Sheet,strip,plate),4.1.6 Edge(Section 15),4.1.7 Dimensions(size,thickness,wid