1、Designation:A92205(Reapproved 2015)Standard Specification forSilicon Metal1This standard is issued under the fixed designation A922;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of last revision.A number in parentheses ind
2、icates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This specification covers several grades of silicon metal.1.2 The values stated in inch-pound units are to be regardedas standard.The values given in parentheses ar
3、e mathematicalconversions to SI units that are provided for information onlyand are not considered standard.The SI equivalents of inch-pound units given may be approximate.2.Referenced Documents2.1 ASTM Standards:2A1025 Specification for Ferroalloys and Other AlloyingMaterials,General RequirementsE1
4、1 Specification for Woven Wire Test Sieve Cloth and TestSievesE50 Practices for Apparatus,Reagents,and Safety Consid-erations for Chemical Analysis of Metals,Ores,andRelated MaterialsE60 Practice for Analysis of Metals,Ores,and RelatedMaterials by SpectrophotometryE360 Test Methods for Chemical Anal
5、ysis of Silicon andFerrosilicon(Withdrawn 2006)33.General Conditions for Delivery3.1 Materials furnished to this specification shall conform tothe requirements of Specification A1025,including any supple-mentary requirements that are indicated in the purchase order.Failure to comply with the general
6、 requirements of Specifica-tion A1025 constitutes nonconformance with this specification.In case of conflict between the requirements of this specifica-tion and Specification A1025,this specification shall prevail.4.Chemical Composition4.1 The grades shall conform to the requirements as to thechemic
7、al composition specified in Table 1.4.2 The manufacturer shall furnish an analysis of eachshipment showing the percentage of each element specified.4.3 Upon request of the purchaser,the manufacturer shallfurnish an analysis of any trace elements on a schedulemutually agreed upon between the supplier
8、 and the purchaser.5.Size5.1 The various grades are available in sizes listed in Table2.5.2 The sizes listed in Table 2 are typical as shipped fromthe manufacturers plant.The various grades can exhibitdifferent degrees of friability;therefore some attrition may beexpected in transit,storage,and hand
9、ling.A quantitative test isnot available for rating relative friability of silicon metal.Acode system has been developed,therefore,for this purpose,and a number rating for each product type is shown in Table 3.Definitions applicable to these code numbers are given inSpecification A1025.6.Chemical An
10、alysis6.1 The chemical analysis of the material shall be made inaccordance with the procedure for silicon metal as described inTest Methods E360 or alternative methods that will yieldequivalent results.6.2 If alternative methods of analysis are used,in case ofdiscrepancy,Test Methods E360 shall be u
11、sed for referee.6.3 Where a method is not given in Test Methods E360 forthe analysis for a particular element,the analysis shall be madein accordance with a procedure agreed upon between themanufacturer and the purchaser.NOTE1For further information,see Practices E50 and E60.7.Keywords7.1 silicon;si
12、licon metal1This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys and is the direct responsibility of SubcommitteeA01.18 on Castings.Current edition approved Nov.1,2015.Published November 2015.Originallyapproved in 1993.Last previous edition a
13、pproved in 2010 as A922 05(2010).DOI:10.1520/A0922-05R15.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.3The last
14、 approved version of this historical standard is referenced onwww.astm.org.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United States1 ASTM International takes no position respecting the validity of any patent rights asserted in connection with any i
15、tem mentionedin this standard.Users of this standard are expressly advised that determination of the validity of any such patent rights,and the riskof infringement of such rights,are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical commi
16、ttee and must be reviewed every five years andif not revised,either reapproved or withdrawn.Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters.Your comments will receive careful consideration at a meeting of theresponsible technical committee,which you may attend.If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards,at the