1、Designation:B483/B483M131Standard Specification forAluminum and Aluminum-Alloy Drawn Tube and Drawn Pipefor General Purpose Applications1This standard is issued under the fixed designation B483/B483M;the number immediately following the designation indicates the yearof original adoption or,in the ca
2、se of revision,the year of last revision.A number in parentheses indicates the year of last reapproval.A superscript epsilon()indicates an editorial change since the last revision or reapproval.1NOTETable 1 was corrected editorially in June 2014.1.Scope*1.1 This specification covers aluminum and alu
3、minum-alloydrawn tube and drawnpipe in straight lengths and tube in coilsfor general purpose applications in the alloys(Note 2),andtempers shown in Tables 1 and 2.Coiled tubes are generallyavailable only as round tubes with a wall thickness notexceeding 0.083 in.2.00 mm and only in non-heat-treatabl
4、ealloys.NOTE1For drawn seamless tubes,see Specifications B210 andB210M,for tubes to be used in condensers and heat exchangers,Specifications B234 and B234M,and for seamless pipe,SpecificationB241/B241M.For extruded structural tube and pipe,see SpecificationB429.NOTE2this specification use of the ter
5、m alloy in the general senseincludes aluminum as well as aluminum alloy.1.2 Alloy and temper designations are in accordance withANSI H35.1/H35.1(M).The equivalent Unified Number Sys-tem alloy designations are those of Table 3 preceded byA9,forexample A91060 for aluminum 1060 in accordance withPracti
6、ce E527.1.3 For acceptance criteria for inclusion of new aluminumand aluminum alloys in this specification,see Annex A2.1.4 The values stated in either inch-pound units or SI unitsare to be regarded separately as standard.Within the text,theSI units are shown in brackets.The values stated in eachsys
7、tem may not be exact equivalents;therefore,each systemshall be used independently of the other.Combining valuesfrom the two systems may result in nonconformance with thestandard.1.5 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibi
8、lity of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2.Referenced Documents2.1 The following documents of the issue in effect on dateof order acceptance form a part of this specification to the
9、extent referenced herein:2.2 ASTM Standards:2B210 Specification for Aluminum and Aluminum-AlloyDrawn Seamless TubesB210M Specification for Aluminum and Aluminum-AlloyDrawn Seamless Tubes(Metric)B234 Specification for Aluminum and Aluminum-AlloyDrawn Seamless Tubes for Condensers and Heat Ex-changers
10、B234M Specification for Aluminum and Aluminum-AlloyDrawn Seamless Tubes for Condensers and Heat Ex-changers(Metric)B241/B241M Specification for Aluminum and Aluminum-Alloy Seamless Pipe and Seamless Extruded TubeB429 Specification forAluminum-Alloy Extruded StructuralPipe and TubeB557 Test Methods f
11、or Tension Testing Wrought and CastAluminum-and Magnesium-Alloy ProductsB557M Test Methods for Tension Testing Wrought and CastAluminum-and Magnesium-Alloy Products(Metric)B597 Practice for Heat Treatment of Aluminum Alloys(Withdrawn 2002)3B660 Practices for Packaging/Packing of Aluminum andMagnesiu
12、m ProductsB666/B666M Practice for Identification Marking of Alumi-num and Magnesium ProductsB881 Terminology Relating to Aluminum-and Magnesium-Alloy ProductsB918 Practice for Heat Treatment of Wrought AluminumAlloysE29 Practice for Using Significant Digits in Test Data to1This specification is unde
13、r the jurisdiction of ASTM Committee B07 on LightMetals and Alloys and is the direct responsibility of Subcommittee B07.03 onAluminum Alloy Wrought Products.Current edition approved May 1,2013.Published June 2013.Originallyapproved in 1983.Last previous edition approved in 2003 as B483/B483M03,which
14、 was withdrawn January 2012 and reinstated in May 2013.DOI:10.1520/B0483_B0483M-13E01.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page
15、 onthe ASTM website.3The last approved version of this historical standard is referenced onwww.astm.org.*A Summary of Changes section appears at the end of this standardCopyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United States1 TABLE 1 Tensile Prope
16、rty Limits,TubeA,BALLOYANDTEMPERSPECIFIED WALLTHICKNESSin.mmTENSILE STRENGTH-ksi MPaElongation in 2 in.50 mm or4 Diameter,Cmin,%JULTIMATEYIELDD(0.2%Offset),ksi MPaFULLSECTIONSPECIMENECut-Out SpecimenFmin.max.min.max.In 50 mmIn 5Diameter(5.65=A)G1060F,I1060-O0.010-0.500 0.25-12.508.5 6013.5 952.5 15.1060-H120.010-0.500 0.25-12.5010.0 70.4.0 30.1060-H140.010-0.500 0.25-12.5012.0 85.10.0 70.1060-H180.010-0.500 0.25-12.5016.0 110.13.0 90.1060-H113K0.010-0.500.025-12.508.5 60.2.5 15.1100F,I1100-O0.01