1、Designation:A717/A717M12(Reapproved 2018)Standard Test Method forSurface Insulation Resistivity of Single-Strip Specimens1This standard is issued under the fixed designation A717/A717M;the number immediately following the designation indicates the yearof original adoption or,in the case of revision,
2、the year of last revision.A number in parentheses indicates the year of last reapproval.A superscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This test method covers a means of testing the surfaceinsulation resistivity of single strips or punchings of
3、flat-rolledelectrical steel under predetermined conditions of voltage,pressure,and temperature.1.2 The values stated in either SI units or inch-pound unitsare to be regarded separately as standard.The values stated ineach system may not be exact equivalents;therefore,eachsystem shall be used indepen
4、dently of the other.Combiningvalues from the two systems may result in non-conformancewith the standard.1.3 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,
5、and environmental practices and deter-mine the applicability of regulatory limitations prior to use.1.4 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of Internationa
6、l Standards,Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2A34/A34M Practice for Sampling and Procurement Testingof Magnetic Materials3.Terminology3.1 Definitions of Terms Specific to This Standard
7、:3.1.1 surface insulation resistivityrefers to the effectiveresistivity of a single insulative layer tested between appliedbare metal contacts and the base metal of the insulated testspecimen.It is not the same as the terms interlaminar resistivityand stack resistivity,which refer to the average res
8、istivity oftwo adjacent insulative surfaces in contact with each other.3.1.2 The apparatus is popularly known as a Franklin tester.4.Summary of Test Method4.1 Ten metallic contacts of fixed area are applied to one ofthe surfaces of the specimen and electrical contact is made withthe base metal by tw
9、o drills.The effectiveness of the surfaceinsulation is then indicated by a measurement of averageelectrical current flowing between the contacts and the basemetal under specified applied voltage.This measurement canbe used directly as an indicator of insulation quality or may beconverted to an appar
10、ent surface insulation resistivity value.5.Significance and Use5.1 This test method is particularly suitable for qualitycontrol in the application of insulating coatings.5.2 Surface insulation resistivity is evaluated from a dccurrent that can range from 0(perfect insulator)to 1 A(perfectconductor).
11、5.3 Single readings should not be considered significantsince the nature of the test device and specimen are such thatsuccessive measurements of a specimen often yield differentvalues.6.Apparatus6.1 The apparatus,as shown in Fig.1 and Fig.2,shallconsist of a contact unit or test head which is attach
12、ed to thehead of a hydraulic press.Its associated measuring equipment,which may be remotely located,includes an ammeter,voltmeter,and voltage regulated dc power supply.Whenmeasurements are to be made at elevated temperatures,theplaten beneath the specimen is heated and controlled.Detaileddescription
13、s of the various components are given in AnnexA1.7.Sampling7.1 Samples shall be representative of the steel and shall becut in a manner to assure representative sampling as describedin Practice A34/A34M.1This test method is under the jurisdiction of ASTM Committee A06 onMagnetic Properties and is th
14、e direct responsibility of Subcommittee A06.01 on TestMethods.Current edition approved May 1,2018.Published June 2018.Originallyapproved in 1975.Last previous edition approved in 2012 as A717/A717M 12.DOI:10.1520/A0717_A0717M-12R18.2For referenced ASTM standards,visit the ASTM website,www.astm.org,o
15、rcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standar
16、d was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.1 8.Test Specimen8.1 The width and length of a specimen strip shall be greaterthan the width and length respectively of the assembly ofcontacts.The suggested minimum specimen size is 2 by 5 in.50 by 130 mm.8.2 A