1、Designation:D7332/D7332M22Standard Test Method forMeasuring the Fastener Pull-Through Resistance of aFiber-Reinforced Polymer Matrix Composite1This standard is issued under the fixed designation D7332/D7332M;the number immediately following the designation indicates theyear of original adoption or,i
2、n the case of revision,the year of last revision.A number in parentheses indicates the year of lastreapproval.A superscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This test method determines the fastener pull-throughresistance of multidirectional poly
3、mer matrix composites rein-forced by high-modulus fibers.Fastener pull-through resis-tance is characterized by the force-versus-displacement re-sponse exhibited when a mechanical fastener is pulled througha composite plate,with the force applied perpendicular to theplane of the plate.The composite m
4、aterial forms are limited tocontinuous-fiber or discontinuous-fiber(tape or fabric,or both)reinforced composites for which the laminate is symmetric andbalanced with respect to the test direction.The range ofacceptable test laminates and thicknesses is defined in 8.2.1.2 Two test procedures and conf
5、igurations are provided.The first,Procedure A,is suitable for screening and fastenerdevelopmentpurposes.Thesecond,ProcedureB,isconfiguration-dependent and is suitable for establishing designvalues.Both procedures can be used to perform comparativeevaluations of candidate fasteners/fastener system de
6、signs.1.3 The specimens described herein may not be representa-tive of actual joints which may contain one or more free edgesadjacent to the fastener,or may contain multiple fasteners thatcan change the actual boundary conditions.1.4 This test method is consistent with the recommendationsof CMH-17,w
7、hich describes the desirable attributes of afastener pull-through test method.1.5 UnitsThe values stated in either SI units or inch-pound units are to be regarded separately as standard.Thevalues stated in each system are not necessarily exact equiva-lents;therefore,to ensure conformance with the st
8、andard,eachsystem shall be used independently of the other,and valuesfrom the two systems shall not be combined.1.5.1 Within the text,the inch-pound units are shown inbrackets.1.6 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibili
9、ty of the user of this standard to establish appro-priate safety,health,and environmental practices and deter-mine the applicability of regulatory limitations prior to use.1.7 This international standard was developed in accor-dance with internationally recognized principles on standard-ization esta
10、blished in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2D792 Test Methods for Density and Specific Gravity(Rela-tive Densi
11、ty)of Plastics by DisplacementD883 Terminology Relating to PlasticsD2584 Test Method for Ignition Loss of Cured ReinforcedResinsD2734 Test Methods for Void Content of Reinforced PlasticsD3171 Test Methods for Constituent Content of CompositeMaterialsD3410/D3410M Test Method for Compressive Propertie
12、s ofPolymer Matrix Composite Materials with UnsupportedGage Section by Shear LoadingD3878 Terminology for Composite MaterialsD5229/D5229M Test Method for MoistureAbsorption Prop-erties and Equilibrium Conditioning of Polymer MatrixComposite MaterialsD5687/D5687M Guide for Preparation of Flat Composi
13、tePanels with Processing Guidelines for Specimen Prepara-tionE4 Practices for Force Calibration and Verification of Test-ing MachinesE6 Terminology Relating to Methods of Mechanical TestingE18 Test Methods for Rockwell Hardness of Metallic Ma-terialsE122 Practice for Calculating Sample Size to Estim
14、ate,WithSpecified Precision,the Average for a Characteristic of aLot or Process1This test method is under the jurisdiction of ASTM Committee D30 onComposite Materials and is the direct responsibility of Subcommittee D30.05 onStructural Test Methods.Current edition approved May 1,2022.Published May 2
15、022.Originallyapproved in 2007.Last previous edition approved in 2016 as D7332/D7332M 16.DOI:10.1520/D7332_D7332M-22.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the
16、standards Document Summary page onthe ASTM website.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.1E177 Practice for Use of t