1、Designation:D759419Standard Test Method forDetermining Fretting Wear Resistance of LubricatingGreases Under High Hertzian Contact Pressures Using aHigh-Frequency,Linear-Oscillation(SRV)Test Machine1This standard is issued under the fixed designation D7594;the number immediately following the designa
2、tion indicates the year oforiginal adoption or,in the case of revision,the year of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope*1.1 This test method covers a procedure for
3、 determining thelubricating action of greases in order to prevent“fretting”wearunder linear oscillation with associated low strokes and highHertzian contact pressures under high-frequency linear-oscillation motion using the SRV test machine.By performingadditional,nonmandatory extreme-pressure tests
4、 in accordancewith Test Method D5706,the test grease should be shown to beable to withstand a Hertzian contact pressure of at least2200 MPa without adhesive failure.1.2 The values stated in SI units are to be regarded asstandard.No other units of measurement are included in thisstandard.1.3 This sta
5、ndard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practices and deter-mine the applicability of regulatory limitations prior to use.1.4 This interna
6、tional standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Commit
7、tee.2.Referenced Documents2.1 ASTM Standards:2A295/A295M Specification for High-Carbon Anti-FrictionBearing SteelD217 Test Methods for Cone Penetration of LubricatingGreaseD235 Specification for Mineral Spirits(Petroleum Spirits)(Hydrocarbon Dry Cleaning Solvent)D4175 Terminology Relating to Petrole
8、um Products,LiquidFuels,and LubricantsD5706 Test Method for Determining Extreme PressureProperties of Lubricating Greases Using a High-Frequency,Linear-Oscillation(SRV)Test MachineD6425 Test Method for Measuring Friction and Wear Prop-erties of Extreme Pressure(EP)Lubricating Oils UsingSRV Test Mach
9、ineD7421 Test Method for Determining Extreme PressureProperties of Lubricating Oils Using High-Frequency,Linear-Oscillation(SRV)Test MachineD7755 Practice for Determining the Wear Volume on Stan-dard Test Pieces Used by High-Frequency,Linear-Oscillation(SRV)Test MachineE45 Test Methods for Determini
10、ng the Inclusion Content ofSteelG40 Terminology Relating to Wear and Erosion2.2 Other Standards:3DIN 51834-3:2008-12 Testing of LubricantsTribologicalTest in Translatory Oscillation ApparatusPart 3:Deter-mination of Tribological Behaviour of Materials in Coop-eration with LubricantsDIN51631:1999 Spe
11、cial-Boiling-PointSpiritsRequirements and TestingDIN EN ISO 683-17 Heat-Treated Steels,Alloy Steels andFree-Cutting SteelsPart 17:Ball and Roller BearingSteels Replaces DIN 17230-1980DIN EN ISO 13565-2:1998 Geometrical Product Specifica-tions(GPS)Surface Texture:Profile MethodSurfacesHaving Stratifi
12、ed Functional PropertiesPart 2:HeightCharacterization Using the Linear Material Ratio CurveReplaces DIN 4776-19903.Terminology3.1 Definitions:1This test method is under the jurisdiction of ASTM Committee D02 onPetroleum Products,Liquid Fuels,and Lubricants and is the direct responsibility ofSubcommi
13、ttee D02.G0.04 on Functional Tests-Tribology.Current edition approved Dec.1,2019.Published January 2020.Originallyapproved in 2010.Last previous edition approved in 2016 as D7594 16.DOI:10.1520/D7594-19.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Servic
14、e at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.3Available from Available from Beuth Verlag GmbH(DIN-DIN DeutschesInstitut fur Normung e.V.),Burggrafenstrasse 6,10787,Berlin,Germany,http:/www.en.din.de.*A Summar
15、y of Changes section appears at the end of this standardCopyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the
16、 Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.3.1.1 break-in,nin tribology,an initial transition processoccurring in newly established wearing contacts,often accom-panied by transients in coefficient of friction or wear rate,orboth,that are uncharacteristic of the given tribological systemslong-term behavior.G403.1.2 coeffcient of friction,or,nin tribology,thedimens