1、Designation:D7264/D7264M21Standard Test Method forFlexural Properties of Polymer Matrix Composite Materials1This standard is issued under the fixed designation D7264/D7264M;the number immediately following the designation indicates theyear of original adoption or,in the case of revision,the year of
2、last revision.A number in parentheses indicates the year of lastreapproval.A superscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This test method determines the flexural stiffness andstrength properties of polymer matrix composites.1.1.1 Procedure AA t
3、hree-point loading system utilizingcenter loading on a simply supported beam.1.1.2 Procedure BA four-point loading system utilizingtwo load points equally spaced from their adjacent supportpoints,with a distance between load points of one-half of thesupport span.NOTE1Unlike Test Method D6272,which a
4、llows loading at bothone-third and one-half of the support span,in order to standardizegeometry and simplify calculations,this standard permits loading at onlyone-half the support span.1.2 For comparison purposes,tests may be conducted ac-cording to either test procedure,provided that the sameproced
5、ure is used for all tests,since the two proceduresgenerally give slightly different property values.1.3 UnitsThe values stated in either SI units or inch-pound units are to be regarded separately as standard.Thevalues stated in each system are not necessarily exact equiva-lents;therefore,to ensure c
6、onformance with the standard,eachsystem shall be used independently of the other,and valuesfrom the two systems shall not be combined.1.4 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establi
7、sh appro-priate safety,health,and environmental practices and deter-mine the applicability of regulatory limitations prior to use.1.5 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for
8、theDevelopment of International Standards,Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2D790 Test Methods for Flexural Properties of Unreinforcedand Reinforced Plastics and Electrical Insulating M
9、ateri-alsD792 Test Methods for Density and Specific Gravity(Rela-tive Density)of Plastics by DisplacementD883 Terminology Relating to PlasticsD2344/D2344M Test Method for Short-Beam Strength ofPolymer Matrix Composite Materials and Their LaminatesD2584 Test Method for Ignition Loss of Cured Reinforc
10、edResinsD2734 Test Methods for Void Content of Reinforced PlasticsD3171 Test Methods for Constituent Content of CompositeMaterialsD3878 Terminology for Composite MaterialsD5229/D5229M Test Method for MoistureAbsorption Prop-erties and Equilibrium Conditioning of Polymer MatrixComposite MaterialsD568
11、7/D5687M Guide for Preparation of Flat CompositePanels with Processing Guidelines for Specimen Prepara-tionD6272 Test Method for Flexural Properties of Unreinforcedand Reinforced Plastics and Electrical Insulating Materi-als by Four-Point BendingD6856 Guide for Testing Fabric-Reinforced“Textile”Com-
12、posite MaterialsE4 Practices for Force Verification of Testing MachinesE6 Terminology Relating to Methods of Mechanical TestingE122 Practice for Calculating Sample Size to Estimate,WithSpecified Precision,the Average for a Characteristic of aLot or ProcessE177 Practice for Use of the Terms Precision
13、 and Bias inASTM Test MethodsE456 Terminology Relating to Quality and Statistics2.2 Other Documents:3ANSIY14.5-1999 DimensioningandTolerancingIncludes Inch and Metric1This test method is under the jurisdiction of ASTM Committee D30 onComposite Materials and is the direct responsibility of Subcommitt
14、ee D30.04 onLamina and Laminate Test Methods.Current edition approved Jan.1,2021.Published February 2021.Originallyapproved in 2006.Last previous edition approved in 2015 as D7264/D7264M 15.DOI:10.1520/D7264_D7264M-21.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM
15、Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.3Available from American National Standards Institute(ANSI),25 W.43rd St.,4th Floor,New York,NY 10036,http:/www.ansi.org.Copyright ASTM Internationa
16、l,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.1ANSI B46.1-1995 Surface Texture(Surface Roughness,Waviness and Lay)3.Terminology3.1 DefinitionsTerminolo