1、Designation:D5683/D5683M95(Reapproved 2022)Standard Test Method forFlexibility of Roofing and Waterproofing Materials andMembranes1This standard is issued under the fixed designation D5683/D5683M;the number immediately following the designation indicates theyear of original adoption or,in the case o
2、f revision,the year of last revision.A number in parentheses indicates the year of lastreapproval.A superscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This test method measures the flexibility of roofing orwaterproofing sheet materials or membranes by
3、 bending thetest material over a block containing arcs of specific radii at astandard temperature.1.2 The values stated in either SI units or inch-pound unitsare to be regarded separately as standard.The values stated ineach system may not be exact equivalents;therefore,eachsystem shall be used inde
4、pendently of the other.Combiningvalues from the two systems may result in nonconformancewith the standard.1.3 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,healt
5、h,and environmental practices and deter-mine the applicability of regulatory limitations prior to use.1.4 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of Internatio
6、nal Standards,Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2D1079 Terminology Relating to Roofing and Waterproofing3.Terminology3.1 For definitions of terms used in this test method,refer toTermin
7、ology D1079.4.Summary of Test Method4.1 Bend the five specimens of roofing or waterproofingsheet materials or membrane,conditioned at 4.4 C 40 F(see Note 1),over a block(see Fig.1)designed to provide arcsof equal length with 6 mm 14in.,13 mm 12in.,19 mm34in.,and 25 mm 1 in.radii,and the smallest rad
8、ius isreported where cracking is not observed in any specimen.NOTE1Other test temperatures may be used in addition to the testsrequired at 4.4 C 40 F,and refrigerated conditioning chambers may beused instead of the water bath specified.Follow procedures outlined inSection 8 if refrigerated chamber i
9、s utilized;however,the plastic bag maybe omitted.5.Significance and Use5.1 This test method is designed to aid those interested inthe engineering properties of roofing and waterproofing sheetmaterials and membranes.5.2 This test method enables a researcher to measure therelative flexibility of roofi
10、ng and waterproofing sheet materialsand membranes under standard conditions in the laboratory.5.3 The data obtained from this test method will not permitprediction of the service life of a membrane.Membraneflexibility is important during application,and changes inflexibility are believed to be linke
11、d to the performance ofroofing and waterproofing membranes,but the actual linkbetween test data and performance is unknown and is depen-dent on the materials and exposure.6.Apparatus6.1 Water BathA bath with the capacity of at least 10 L2.5 gal and capable of maintaining a temperature of 4.4 60.1 C
12、40 6 0.2 F.6.2 Polyethylene BagsA sealable plastic bag for condi-tioning each group of test specimens.Commercial 1 galsealable polyethylene scrap or food storage bags can performthis function.6.3 Test BlockThe test block(see Fig.1)may be madefrom any hard,durable material that conforms to the dimen-
13、sions shown in Fig.1.It is designed to provide equal arclengths for arcs with 6 mm 14in.,13 mm 12in.,19 mm34in.,and 25 mm 1 in.radii.1This test method is under the jurisdiction ofASTM Committee D08 on Roofingand Waterproofing and is the direct responsibility of Subcommittee D08.20 onRoofing Membrane
14、 Systems.Current edition approved Nov.1,2022.Published November 2022.Originallyapproved in 1995.Last previous edition approved in 2017 as D5683/D5683M 95(2017).DOI:10.1520/D5683_D5683M-95R22.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at service
15、astm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with intern
16、ationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.17.Sampling7.1 This test method requires a total of one 152 by 305 mm6 by 12 in.sample from the sheet material or membrane.7.2 Cut five 25 by 152 mm 1 by 6 in.specimens in themachine direction(the length)and five 1 by 6 in.specimens inthe cross directio