1、Designation:D447308(Reapproved 2021)Standard Test Method forPlastics:Dynamic Mechanical Properties:Cure Behavior1This standard is issued under the fixed designation D4473;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of la
2、st revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S.Department of Defense.1.Scope1.1 This test method covers the use of dynam
3、ic-mechanical-oscillation instrumentation for gathering and reporting thethermal advancement of cure behavior of thermosetting resin.It may be used for determining the cure properties of bothunsupported resins and resins supported on substrates sub-jected to various oscillatory deformations.1.2 This
4、 test method is intended to provide a means fordetermining the cure behavior of supported and unsupportedthermosetting resins over a range of temperatures by freevibration as well as resonant and nonresonant forced-vibrationtechniques,in accordance with Practice D4065.Plots ofmodulus,tan delta,and d
5、amping index as a function oftime/temperature are indicative of the thermal advancement orcure characteristics of a resin.1.3 This test method is valid for a wide range of frequencies,typically from 0.01 to 100 Hz.However,it is stronglyrecommended that low-frequency test conditions,generallybelow 1.
6、5 Hz,be utilized as they generally will result in moredefinitive cure-behavior information.1.4 This test method is intended for resin/substrate compos-ites that have an uncured effective elastic modulus in sheargreater than 0.5 MPa.1.5 Apparent discrepancies may arise in results obtainedunder differ
7、ing experimental conditions.These apparent differ-ences from results observed in another study can usually bereconciled,without changing the observed data,by reporting infull(as described in this test method)the conditions underwhich the data were obtained.1.6 Due to possible instrumentation complia
8、nce,especiallyin the compressive mode,the data generated may indicaterelative and not necessarily absolute property values.1.7 Test data obtained by this test method are relevant andappropriate for use in engineering design.1.8 The values stated in SI units are to be regarded as thestandard.1.9 This
9、 standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practices and deter-mine the applicability of regulatory limitations prior to use.Specific pre
10、cautionary statements are given in Note 5.NOTE1There is no known ISO equivalent to this standard.1.10 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International
11、Standards,Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2D4000 Classification System for Specifying Plastic Materi-alsD4065 Practice for Plastics:Dynamic Mechanical Proper-ties:Determination and Re
12、port of ProceduresD4092 Terminology for Plastics:Dynamic MechanicalPropertiesASTM/IEEE SI10 Standard for Use of the InternationalSystem of Units(SI):The Modern Metric System3.Terminology3.1 DefinitionsFor definitions applicable to this testmethod refer to Terminology D4092.4.Summary of Test Method4.
13、1 A known amount of thermosetting liquid resin or resin-impregnated substrate is placed in mechanical oscillation ateither a fixed or natural resonant frequency or by free vibrationand at either isothermal conditions,with a linear temperatureincrease or using a time-temperature relation simulating a
14、1This test method is under the jurisdiction of ASTM Committee D20 on Plasticsand is the direct responsibility of Subcommittee D20.10 on Mechanical Properties.Current edition approved July 1,2021.Published July 2021.Originally approvedin 1985.Last previous edition approved in 2016 as D4473-08(2016).D
15、OI:10.1520/D4473-08R21.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.*A Summary of Changes section appears at th
16、e end of this standardCopyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.1processing condition.The elastic or loss modulus,or bot