1、Designation:D325804(Reapproved 2014)Standard Test Method forPorosity of White or Near White Paint Films by Staining1This standard is issued under the fixed designation D3258;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of
2、 last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This test method covers the determination of the poros-ity of a white or near white mineral spirits insoluble paint filmto
3、 indicate the degree to which a subsequent coat will pen-etrate.1.2 The texture of the film can affect cleanup that willinfluence the results of the test.Astain applied to a high-hidingpaint will not lower the reflectance as much as the same stainapplied to a low-hiding paint of equal porosity.These
4、 pointsmust be considered in comparing different paints.1.3 The values stated in SI units are to be regarded as thestandard.The values given in parentheses are for informationonly.1.4 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsi
5、bility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2.Referenced Documents2.1 ASTM Standards:2E1347 Test Method for Color and Color-Difference Mea-surement by Tristimulus Colorimetry3.Summar
6、y of Test Method3.1 The test paint is applied to a nonporous surface,airdried,then measured for reflectance.A special colored pen-etrating medium is applied,the excess removed in a specifiedmanner,and reflectance measured again.The difference be-tween the two readings indicates the degree of porosit
7、y;thesmaller the difference,the lower the porosity of the film and thegreater its ability to resist penetration.4.Apparatus and Materials4.1 Film Applicator,150 mm(6 in.)wide with a clearanceof 300 m(12 mils).4.2 Film Applicator,140 mm(512in.)wide with a clearanceof 250 m(10 mils).4.3 Reflectometer,
8、meeting the requirements of Test MethodE1347.4.4 Vacuum Drawdown Plate.4.5 Camelhair Brush(approximately 13 mm(12in.)wide).4.6 Plastic Wash Bottle,containing odorless mineral spirits(about 500 mL(16 oz).4.7 Test PanelSmooth nonporous panel such as sealedwhite,cardboard chart,or white plastic sheet.4
9、.8 Penetrating MediumA composition of pigment anddark-colored dye dispersed in organic liquid vehicle.4.9 Filter Paper.5.Procedure5.1 Place the test panel on the vacuum plate and apply thepaint under test with the 30-m(12-mil)clearance drawdownblade.Remove the test panel from the vacuum plate and ai
10、r dry48 h under standard conditions of 23 6 2C(73 6 3.5F)and50 6 5%relative humidity.5.2 Determine the percent reflectance of the dry film usingthe green filter on the reflectometer.When making this reading,back up the panel with a flat rigid opaque object and mark thearea on which the reading was m
11、ade.5.3 Place the panel containing the dry paint film on thevacuum plate.Using the 25-m(10-mil)clearance blade,applythe penetrating medium over the test paint,covering the areamarked as above and drawing the applicator blade in the samedirection as before.5.4 After 5 min 6 15 s wash off excess penet
12、rating medium.To do this,hold the panel vertically and remove the mediumusing the camelhair brush wet with odorless mineral spirits.Repeat the process until most of the excess is removed.Thencontinue to remove more of the excess by applying mineralspirits directly from the wash bottle to the area ab
13、ove the stainso that it flows across the stained area.Pause to observe thebead that forms at the bottom of the panel.If the bead is not1This test method is under the jurisdiction of ASTM Committee D01 on Paintand Related Coatings,Materials,and Applications and is the direct responsibility ofSubcommi
14、ttee D01.42 on Architectural Coatings.Current edition approved Dec.1,2014.Published December 2014.Originallyapproved in 1973.Last previous edition approved in 2010 as D3258 04(2010)1.DOI:10.1520/D3258-04R10R14.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer
15、 Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United States1 clear,continue washing with mineral spirits un
16、til the bead isessentially clear.Test with filter paper to be sure no dyeremains in the bead.5.5 Hang the panel in a vertical position and air dry for 3 h.As before,read the percent reflectance over the same area ofthe panel with the same flat rigid opaque object behind thepanel.6.Report6.1 Report the difference between the percent reflectance ofthe untested film and that of the penetrated film.7.Precision7.1 On the basis of an interlaboratory study of this testmethod in which one operator in ea