1、Designation:D280511(Reapproved 2018)Standard Test Method forHiding Power of Paints by Reflectometry1This standard is issued under the fixed designation D2805;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of last revision.A
2、 number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S.Department of Defense.INTRODUCTIONUsing equations derived from Kubelka-Munk turbid med
3、ia theory(1-4)2(see Annex A1),thereflectance of a coating can be predicted for any film thickness from measurements made at only one.On this basis several rapid and accurate test methods(5,6)have been developed for determininghiding power.In the past such test methods have been considered difficult
4、due to complexities,apparent and actual,in the treatment of data.The present test method has been simplified in thisrespect,primarily by adapting it fully for computer calculations.Although the use of broad-band reflectometry makes this test method theoretically valid only fornonchromatic(white or g
5、ray)colors,good agreement has been obtained with chromatic paints as well.This is undoubtedly because the experimental measurements are made fairly close to the hiding powerend point so that the Kubelka-Munk extrapolation and thus any associated error is relatively small.This test method is therefor
6、e recommended without restriction as to color.1.Scope1.1 This test method covers the determination,withoutreference to a material paint standard,of the hiding power ofair dry coatings with Y tristimulus values greater than 15%.With appropriate modification,it can also be used to testbaking finishes.
7、1.2 The values stated in SI units are to be regarded asstandard.No other units of measurement are included in thisstandard.1.3 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-pr
8、iate safety,health,and environmental practices and deter-mine the applicability of regulatory limitations prior to use.1.4 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopm
9、ent of International Standards,Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:3D344 Test Method for Relative Hiding Power of Paints bythe Visual Evaluation of BrushoutsD1475 Test Method for Density
10、of Liquid Coatings,Inks,and Related ProductsD3924 Specification for Standard Environment for Condi-tioning and Testing Paint,Varnish,Lacquer,and RelatedMaterials(Withdrawn 2016)4E284 Terminology of AppearanceE1247 Practice for Detecting Fluorescence in Object-ColorSpecimens by SpectrophotometryE1331
11、 Test Method for Reflectance Factor and Color bySpectrophotometry Using Hemispherical GeometryE1347 Test Method for Color and Color-Difference Mea-surement by Tristimulus ColorimetryE1349 Test Method for Reflectance Factor and Color bySpectrophotometry Using Bidirectional(45:0 or 0:45)Geometry3.Term
12、inology3.1 DefinitionsFor definitions used in this test method,seeTerminology E284.1This test method is under the jurisdiction of ASTM Committee D01 on Paintand Related Coatings,Materials,and Applications and is the direct responsibility ofSubcommittee D01.26 on Optical Properties.Current edition ap
13、proved Feb.1,2018.Published February 2018.Originallyapproved in 1969.Last previous edition approved in 2011 as D2805 11.DOI:10.1520/D2805-11R18.2The boldface numbers in parentheses refer to the list of references at the end ofthis standard.3For referenced ASTM standards,visit the ASTM website,www.as
14、tm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.4The last approved version of this historical standard is referenced onwww.astm.org.Copyright ASTM International,100 Barr Harb
15、or Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations i
16、ssued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.1 3.2 Definitions of Terms Specific to This Standard:3.2.1 contrast ratio,nthe ratio of the reflectance of a filmon a black substrate to that of an identical film on a whitesubstrate.3.2.1.1 CW,nthe contrast ratio with a white substrate ofreflectance W.Thus:CW5 R0/RW3.2.1.2 C,nthe contrast ratio with a white substrate forwhich W=0.80.Thus:C 5 R0/R0.803.2.2 reflectance,nthe daylight luminous diffuse reflec-tance facto