1、Designation:D414289(Reapproved 2009)Standard Guide forTesting Epoxy Resins1This standard is issued under the fixed designation D4142;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of last revision.A number in parentheses in
2、dicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This guide covers methods for testing epoxy resins aslisted in Table 1.All of the methods were tested by interlabo-ratory participation in accordance with usual AS
3、TM guide-lines.Each method specifies a recommended amount of samplefor starting a separate analysis,but several of the procedurescan be conducted on the same starting material if so desired.For example,viscosity,color,and density could be run on thesame specimen.1.2 This standard does not purport to
4、 address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2.Referenced Documents2.1 ASTM Standards:2D445 Test Met
5、hod for Kinematic Viscosity of Transparentand Opaque Liquids(and Calculation of Dynamic Viscos-ity)D1209 Test Method for Color of Clear Liquids(Platinum-Cobalt Scale)D1259 Test Methods for Nonvolatile Content of ResinSolutionsD1475 Test Method For Density of Liquid Coatings,Inks,and Related Products
6、D1544 Test Method for Color of Transparent Liquids(Gard-ner Color Scale)D1545 Test Method for Viscosity of Transparent Liquids byBubble Time MethodD1639 Test Method for Acid Value of Organic CoatingMaterials(Withdrawn 2005)3D1652 Test Method for Epoxy Content of Epoxy ResinsD1726 Test Methods for Hy
7、drolyzable Chloride Content ofLiquid Epoxy ResinsD1847 Test Methods for Total Chlorine Content of EpoxyResins(Withdrawn 2007)33.Significance and Use3.1 This guide directs the user to test methods that deter-mine properties generally accepted as standard test items forclassification of epoxy resins.4
8、.Epoxy Content4.1 The epoxy content of epoxy resins is determined byreacting a solution of the resin with a standard solution ofhydrogen bromide in glacial acetic acid.The quantity of acidconsumed is a measure of the epoxy content.Test MethodsD1652 was found to have a repeatability of 2%of the epoxy
9、content and a reproducibility of 6%of the epoxy content.5.Hydrolyzable Chlorine5.1 Test Method D1726 covers the determination of theeasily hydrolyzable chlorine content of liquid epoxy resins inconcentrations below 1 weight%.The specimen is refluxedwith a known amount of a standard alcoholic potassi
10、umhydroxide solution.The amount of hydroxide consumed ismeasured by titration and corresponds to the hydrolyzablechlorine content of the resin.By interlaboratory testing,therepeatability was found to be 0.02%,and the reproducibilitywas found to be 0.05%,both absolute.6.Total Chlorine6.1 Organic and
11、inorganic chlorine compounds are deter-mined in epoxy resins in accordance with Test Methods D1847.The resin specimen is oxidized by combustion in a bombcontaining oxygen under pressure.The chlorides formed aredissolved in a sodium carbonate solution and then eithertitrated or determined gravimetric
12、ally.The absolute repeatabil-ity and reproducibility for the titration method are 0.02 and0.05 weight%,respectively.For the gravimetric method,therepeatability and reproducibility are both reported to be 0.05weight%,absolute.7.Viscosity7.1 Kinematic viscosity is determined by measuring thetime for a
13、 volume of liquid to flow under gravity through a1This guide is under the jurisdiction of ASTM Committee D01 on Paint andRelated Coatings,Materials,and Applications and is the direct responsibility ofSubcommittee D01.33 on Polymers and Resins.Current edition approved Dec.1,2009.Published December 20
14、09.Originallyapproved in 1982.Last previous edition approved in 2001 as D4142 89(2001).DOI:10.1520/D4142-89R09.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standa
15、rds Document Summary page onthe ASTM website.3The last approved version of this historical standard is referenced onwww.astm.org.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United States1 calibrated glass capillary viscometer in accordance with Test
16、Method D445.The dynamic viscosity can be obtained bymultiplying the measured kinematic viscosity by the density ofthe liquid.The limits of precision at the three sigma level ofconfidence were found to be 0.35%relative within onelaboratory and 0.70%relative between laboratories.7.2 It is also possible to measure viscosity by the bubbletime method described in Test Method D1545.The rise time ofa bubble in the resin contained in an ASTM viscosity tube ismeasured.The rise time in seconds is approxim