1、Designation:D318607(Reapproved 2016)Standard Test Methods forRubberEvaluation of SBR(Styrene-Butadiene Rubber)Mixed With Carbon Black or Carbon Black and Oil1This standard is issued under the fixed designation D3186;the number immediately following the designation indicates the year oforiginal adopt
2、ion or,in the case of revision,the year of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 These test methods cover the standard materials,testformula,mixing procedures,an
3、d test methods for the evalua-tion and production control of pigmented types of styrene-butadiene rubbers(SBR).This includes the pigmented SBR oilmasterbatches.1.2 The values stated in SI units are to be regarded as thestandard.The values given in parentheses are for informationonly.1.3 This standar
4、d does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2.Referenced Documents2.1 ASTM Sta
5、ndards:2D412 Test Methods for Vulcanized Rubber and Thermoplas-tic ElastomersTensionD1646 TestMethodsforRubberViscosity,StressRelaxation,andPre-VulcanizationCharacteristics(Mooney Viscometer)D2084 Test Method for Rubber PropertyVulcanizationUsing Oscillating Disk Cure MeterD3182 Practice for RubberM
6、aterials,Equipment,and Pro-cedures for Mixing Standard Compounds and PreparingStandard Vulcanized SheetsD3896 Practice for Rubber From Synthetic SourcesSamplingD4483 Practice for Evaluating Precision for Test MethodStandards in the Rubber and Carbon Black ManufacturingIndustriesD5289 Test Method for
7、 Rubber PropertyVulcanizationUsing Rotorless Cure MetersD6204 Test Method for RubberMeasurement of Unvulca-nized Rheological Properties Using Rotorless Shear Rhe-ometers3.Significance and Use3.1 These test methods are intended mainly for refereepurposes but may be used for quality control of masterb
8、atchproduction.They may also be used in research and develop-ment work and for comparison of different rubber samples in astandard formula.3.2 These test methods may also be used to obtain values forcustomer acceptance of rubber.4.Standard Test Formula4.1 Standard FormulaSee Table 1.5.Sample Prepara
9、tion5.1 Obtain and prepare the test samples in accordance withPractice D3896.6.Mixing Procedures6.1 The compound may be prepared either on a mill,miniature internal mixer,or laboratory internal mixer,althoughslightly different results may be obtained.6.2 Mill Mix Procedure:6.2.1 For general mixing p
10、rocedures,refer to PracticeD3182.6.2.2 Mill Mixing CycleSee Table 2.6.2.2.1 After mixing according to Table 2,measure andrecord the batch mass.If it differs from the theoretical value bymore than 0.5%,discard the batch.6.2.2.2 If required,cut samples from the batch to allowtesting of compound viscos
11、ity and processability in accordancewith Test Methods D1646 or D6204,and vulcanization char-acteristics in accordance with Test Methods D2084 or D5289.6.2.2.3 If tensile stress strain tests are required,sheet off toa finished thickness of approximately 2.2 mm(0.087 in.)andcondition the compound acco
12、rding to Practice D3182.6.3 Miniature Internal Mixer(MIM)Procedure:1These test methods are under the jurisdiction of ASTM Committee D11 onRubber and are the direct responsibility of Subcommittee D11.23 on SyntheticRubbers.Current edition approved June 1,2016.Published July 2016.Originally approvedin
13、 1981.Last previous edition approved in 2011 as D3186 07(2011).DOI:10.1520/D3186-07R16.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary pag
14、e onthe ASTM website.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United States1 6.3.1 For general mixing procedures refer to PracticeD3182.6.3.2 MIM Mixing CycleSee Table 3.6.3.2.1 After mixing according to Table 3,turn off themotor,raise the ram,re
15、move the mixing chamber and dis-charge the batch.Record the maximum batch temperatureindicated,if desired.6.3.2.2 Immediately pass the discharge from the mixertwice through a standard mill maintained at 50 6 5C(122 69F)with a roll separation of 0.5 mm(0.020 in.)once,thentwice at a separation of 3 mm
16、(0.12 in.)in order to dissipateheat.Pass the rolled batch endwise through the mill six timeswith an opening of 0.8 mm(0.032 in.)to enhance thedispersion.6.3.2.3 Measure and record the batch mass.If it differs fromthe theoretical value by more than 0.5%,discard the batch.6.3.2.4 If required,cut samples from the batch to allowtesting of compound viscosity and processability in accordancewith Test Methods D1646 or D6204,and vulcanization char-acteristics in accordance with Test Methods D2084 or D52