1、Designation:D199291(Reapproved 2013)Standard Guide forTesting Synthetic Plasticizers Used in Rubber1This standard is issued under the fixed designation D1992;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of last revision.A
2、 number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This guide covers test methods for synthetic plasticizersthat are used in rubber applications.1.2 This standard does not purport to addres
3、s all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2.Referenced Documents2.1 ASTM Standards:2D70 Test Method for
4、Density of Semi-Solid BituminousMaterials(Pycnometer Method)D92 Test Method for Flash and Fire Points by ClevelandOpen Cup TesterD891 Test Methods for Specific Gravity,Apparent,of LiquidIndustrial ChemicalsD1045 Test Methods for Sampling and Testing PlasticizersUsed in PlasticsD1209 Test Method for
5、Color of Clear Liquids(Platinum-Cobalt Scale)D1218 Test Method for Refractive Index and RefractiveDispersion of Hydrocarbon LiquidsD1544 Test Method for Color of Transparent Liquids(Gard-ner Color Scale)D1962 Test Method for Saponification Value of Drying Oils,Fatty Acids,and Polymerized Fatty Acids
6、(Withdrawn2004)3D2111 Test Methods for Specific Gravity and Density ofHalogenated Organic Solvents and Their AdmixturesD2196 Test Methods for Rheological Properties of Non-Newtonian Materials by Rotational(Brookfield type)ViscometerD2288 Test Method for Weight Loss of Plasticizers onHeating(Withdraw
7、n 2010)3E203 Test Method for Water Using Volumetric Karl FischerTitration3.Significance and Use3.1 Synthetic plasticizers are primarily esters and they areused with the more polar elastomers such as CR or NBR toimprove processing,adjust hardness,and improve low tem-perature properties.These esters m
8、ay be either monomeric orpolymeric and are derived from many different organic acids.3.2 These test methods may be used in establishing andconfirming quality control standards for the synthetic plasticiz-ers used in rubber compounding.It is not implied that the testmethods in this guide are the only
9、 ones of significance,butthese test methods list the properties most commonly specifiedfor ester plasticizers.Other parameters may be needed forspecific application of these materials.4.Sampling4.1 The method of sampling for either tank cars or drums isdescribed in Test Methods D1045.5.Volatility5.1
10、 Volatility is normally measured as mass loss after 2 and24 h when tested at 155C.The procedure is described in TestMethod D2288.6.Moisture6.1 The moisture content should be determined using theKarl Fischer reagent procedure as described in Test MethodE203.7.Acid Number7.1 The acid number,expressed
11、as milligrams of KOH pergram of plasticizer,may be determined from Test MethodsD1045.8.Saponification Number8.1 The saponification value is expressed in milligrams pergram of plasticizer and may be determined by Test MethodD1962.1This guide is under the jurisdiction of ASTM Committee D11 on Rubber a
12、ndis the direct responsibility of Subcommittee D11.20 on Compounding Materials andProcedures.Current edition approved Nov.1,2013.Published January 2014.Originallyapproved in 1991.Last previous edition approved in 2012 as D1992 91(2012).DOI:10.1520/D1992-91R13.2For referenced ASTM standards,visit the
13、 ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.3The last approved version of this historical standard is referenced onwww.astm.org.Copyright ASTM Interna
14、tional,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United States1 9.Color9.1 For clear light colored plasticizers,the APHA platinum-cobalt color standards may be used as described in Test MethodD1209,but for darker or more oily plasticizers,the Gardnercolor standards are necess
15、ary.The Gardner procedure isdescribed in Test Method D1544.10.Specific Gravity10.1 The apparent specific gravity of plasticizers should bereported at 25/25C unless different conditions are mutuallyagreed upon.For low viscosity plasticizers the specific gravitymay be determined using a Westphal balan
16、ce as described inTest Methods D2111 or the hydrometer procedure that isdescribed in Test Methods D891.Plasticizers with mediumviscosity should be tested by the pycnometer procedure asdescribed in Test Methods D891 and highly viscous plasticiz-ers should be tested by the procedure in Test Method D70.11.Viscosity11.1 The viscosity of plasticizers is normally measured at25C by a Brookfield viscometer.The procedure for the test isgiven in Test Methods D2196.12.Refractive Index12.1 The test for refr