1、Designation:D145686(Reapproved 2020)Standard Test Method forRubber PropertyElongation at Specific Stress1This standard is issued under the fixed designation D1456;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of last revis
2、ion.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S.Department of Defense.1.Scope1.1 This test method covers determination of the elo
3、ngationof soft vulcanized rubber compounds under a specified stress.1.2 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practices and dete
4、r-mine the applicability of regulatory limitations prior to use.1.3 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendati
5、ons issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2D1349 Practice for RubberStandard Conditions for Test-ingD3182 Practice for RubberMaterials,Equipment,and Pro-cedures for Mixing Standard Compounds and PreparingStandard Vulc
6、anized SheetsD3183 Practice for RubberPreparation of Pieces for TestPurposes from Products3.Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 piecethe portion of the sample that is prepared fortesting.3.1.2 specific stressforce divided by the cross-sectionalarea of the original spe
7、cimen.4.Summary of Test Method4.1 The test method starts with a piece taken from thesample and includes:(1)the preparation of the specimen and(2)measurement of the elongation of the specimen subjected toa prescribed stress for a specified period of time.The stress isapplied by suspension of a known
8、mass which,under gravity,gives the desired stress.5.Significance and Use5.1 This test method is useful for determining the variabilityin material and the influence of parameters affecting thestress-strain properties of rubber vulcanizates,for example,temperature,relative humidity,preconditioning of
9、rubber,andso forth.This test method is particularly useful for theevaluation of compounding materials used for reference pur-poses.6.Apparatus6.1 Testing MachineTests shall be made on a power-driven machine complying with the following requirements:The machine shall be capable of extending the speci
10、men at auniform speed of between 75 and 90 mm/s(15 and 18 ft/min)until the mass is freely suspended.It shall be equipped with atiming device that automatically starts the instant the mass isfreely suspended by the specimen and signals the operatorwhen the elongation is to be measured.The machine sha
11、ll havea millimetre scale and an indicating device so that elongationmeasurements to the nearest millimetre can be made withoutparallax.A holder shall be attached to the lower grip so thatmasses may be added,preferably by an automatic device,toobtain the desired stress.The masses shall correspond to
12、multiples of the force required for 0.01-mm thickness of thespecimen and shall be accurate within the force required for0.002-mm thickness of the specimen.The grips that hold thespecimen in the tester shall be of a type that tightens automati-cally as the applied tension increases and exerts a unifo
13、rmpressure across the gripping surfaces.A satisfactory tester,including die and thickness gage,is shown in Fig.1.6.2 DieThe die shall be capable of cutting straight speci-mens with parallel sides,approximately 150 mm(6 in.)longand within 60.02 mm(60.001 in.)of the specified width forthe specimens(se
14、e 7.1)at any point along their length.A1This test method is under the jurisdiction of ASTM Committee D11 on Rubberand Rubber-like Materials and is the direct responsibility of Subcommittee D11.10on Physical Testing.Current edition approved Feb.1,2020.Published February 2020.Originallyapproved in 195
15、7.Last previous edition approved in 2014 as D1456 86(2014).DOI:10.1520/D1456-86R20.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page on
16、the ASTM website.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.suitable die is shown in Fig.2.This die consists of six strip