1、Designation:D 1673 94(Reapproved 2004)An American National StandardStandard Test Methods forRelative Permittivity And Dissipation Factor of ExpandedCellular Polymers Used For Electrical Insulation1This standard is issued under the fixed designation D 1673;the number immediately following the designa
2、tion indicates the year oforiginal adoption or,in the case of revision,the year of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon(e)indicates an editorial change since the last revision or reapproval.INTRODUCTIONAlthough fundamentally similar to test
3、 methods used for solid electrical insulating materials in sheetor plate form,certain modifications in the procedures and measurement techniques are necessary forthe proper determination of the relative permittivities and dissipation factors of foamed or expandedcellular polymers.This is occasioned
4、by the fact that in many,if not most,instances expanded cellularmaterials have surfaces that preclude the use of conventional electrodes such as metal foil attached bypetrolatum and similar adhesives,or conducting silver paint applied by brushing or spraying.Furthermore,it is generally true that sla
5、bs or plates of expanded cellular materials are available onlyin substantially greater thicknesses than those commonly used for test specimens of solid insulation.1.Scope1.1 These test methods cover procedures for determiningthe relative permittivities and dissipation factor of flat sheets orslabs o
6、f expanded cellular polymers of both the rigid andflexible types,at frequencies from 60 Hz to 100 MHz.Provision is made for measurements on specimens up to 50mm(2 in.)in thickness,but it is recommended that specimensgreater than 25 mm(1 in.)in thickness shall be tested atfrequencies up to a maximum
7、of only about 1 MHz.1.2 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to us
8、e.2.Referenced Documents2.1 ASTM Standards:2D 150 Test Methods for AC Loss Characteristics and Per-mittivity(Dielectric Constant)of Solid Electrical Insula-tionD 374 Test Methods for Thickness of Solid Electrical Insu-lationD 1056 Specification for Flexible Cellular MaterialsSponge or Expanded Rubbe
9、rD 1711 Terminology Relating to Electrical Insulation3.Terminology3.1 For definitions of relative permittivity,dissipation fac-tor,and loss index,refer to Test Methods D 150 or Terminol-ogy D 1711.4.Significance and Use4.1 Relative Permittivity:4.1.1 Because a relatively large proportion of their vo
10、lumesare composed of more or less uniformly distributed,isolated,orinterconnected gas-filled cells,foamed or expanded cellularpolymers always have lower relative permittivities,at a givenfrequency and temperature,than the solid base resins fromwhich they are prepared.4.1.2 The relative permittivitie
11、s of expanded cellular poly-mers are important because they determine the increase incapacitance between conductors,or between conductors andground,that will result when a circuit or component isencapsulated in such a material,over their correspondingvalues before encapsulation(when air is the surro
12、undingmedium).Likewise,the relative permittivities of an expandedcellular polymer may serve as a measure of the decrease ofsuch capacitances caused by substitution of the expandedmaterial for a solid encapsulating compound or resin of knownrelative permittivity.4.1.3 In transmission lines,such as co
13、axial cable,televisionlead-in cables,and so forth,the reduction of relative permit-tivity of an expanded material from its value in the originalsolid state has significant usefulness in design,since the1These test methods are under the jurisdiction of ASTM Committee D09 onElectrical and Electronic I
14、nsulating Materials and are the direct responsibility ofSubcommittee D 09.12 on Electrical Tests.Current edition approved March 1,2004.Published March 2004.Originallyapproved in 1959.Last previous edition approved in 1998 as D 1673 79(1998).2For referenced ASTM standards,visit the ASTM website,www.a
15、stm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959,United States.capacitance per
16、 foot of cable,and such cable characteristics asvelocity of propagation and characteristic impedance are alldependent upon the relative permittivity of the insulatingmaterial.4.1.4 In wave guides,radomes,dielectric lenses,and soforth,for use at radio frequencies,if the cellular polymer isnonmagnetic,the relative permittivity(usually in combinationwith the dissipation factor)determines such transmissioncharacteristics as velocity of propagation,attenuation distance,decibel loss per meter,phase fa