1、Designation:C1177/C1177M13Standard Specification forGlass Mat Gypsum Substrate for Use as Sheathing1This standard is issued under the fixed designation C1177/C1177M;the number immediately following the designation indicates the yearof original adoption or,in the case of revision,the year of last rev
2、ision.A number in parentheses indicates the year of last reapproval.A superscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope*1.1 This specification covers glass mat gypsum substrate,which is designed to be used as an exterior substrate for aweather barrier.1
3、.2 The values stated in either SI units or inch-pound unitsare to be regarded separately as standard.Within the text,theSI units are shown in brackets.The values stated in eachsystem may not be exact equivalents;therefore,each systemshall be used independently of the other.Combining valuesfrom the t
4、wo systems may result in non-conformance with thestandard.1.3 The text of this standard references notes and footnotesthat provide explanatory material.These notes and footnotes(excluding those in tables and figures)shall not be consideredas requirements of the standard.2.Referenced Documents2.1 AST
5、M Standards:2C11 Terminology Relating to Gypsum and Related BuildingMaterials and SystemsC22 Specification for GypsumC473 Test Methods for Physical Testing of Gypsum PanelProductsC645 Specification for Nonstructural Steel Framing Mem-bersC1264 Specification for Sampling,Inspection,Rejection,Certific
6、ation,Packaging,Marking,Shipping,Handling,and Storage of Gypsum Panel ProductsE119 Test Methods for Fire Tests of Building Constructionand Materials3.Terminology3.1 Definitions shall be in accordance with TerminologyC11.3.2 Definitions of Terms Specific to This Standard:3.2.1 glass mat,na mat of gla
7、ss fibers with or without abinder.3.2.2 edge,nthe bound edge as manufactured.3.2.3 weather barrier,na material that prevents the pas-sage of rain,sleet and snow.4.Materials and Manufacture4.1 Glass Mat Gypsum Substrate shall consist of a noncom-bustible water-resistant core,essentially gypsum comply
8、ingwith Specification C22,surfaced with glass mat partially,orcompletely embedded in the core.4.2 Glass Mat Gypsum Substrate,type X(special fire-resistant)designates glass mat gypsum substrate complyingwith this specification that provide not less than 1-h fireresistance rating for substrate58in.15.
9、9 mm thick or34-hfire resistance rating for substrate12in.12.7 mm thick,applied parallel with and on each side of load bearing 2 by 4wood studs spaced 16 in.406 mm on center with 6d coatednails,178in.48 mm long,0.0915 in.2.3 mm diametershank,14in.6.4 mm diameter heads,spaced 7 in.178 mmon center wit
10、h glass mat gypsum substrate joints staggered 16in.406 mm on each side of the partition and tested inaccordance with Test Methods E119.NOTE1Consult manufacturers for independent test data on assemblydetails and fire resistance ratings for other types of construction.See firetest reports or listings
11、from recognized fire testing laboratories forassembly particulars,materials,and ratings.5.Physical Properties5.1 Specimens shall be taken from the samples obtained inaccordance with Specification C1264.5.2 Specimens shall be tested in accordance with MethodsC473.5.2.1 Flexural StrengthThe specimens
12、shall be tested faceup and face down.The average breaking load shall not be lessthan the following:1This specification is under the jurisdiction of ASTM Committee C11 onGypsum and Related Building Materials and Systems and is the direct responsibilityof Subcommittee C11.01 on Specifications and Test
13、 Methods for Gypsum Products.Current edition approved Oct.1,2013.Published October 2013.Originallyapproved in 1991.Last previous edition approved in 2008 as C1177/C1177M08.DOI:10.1520/C1177_C1177M-13.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service a
14、t serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.*A Summary of Changes section appears at the end of this standardCopyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United
15、 States1 Method BThickness,in.mmLoad,lbf N Bearingedges perpendicular tothe substrate edgeLoad,lbf N Bearing edgesparallel to the substrateedge146.450 22240 17871611.188 39470 3141212.7100 44580 3565815.9140 623100 4455.2.2 Humidified DeflectionSpecimens shall have an av-erage deflection of not more
16、 than the following:Thickness,in.mmHumidified deflection,eighths of an in.mm146.4not required71611.13 91212.72 65815.91 35.2.3 Core,End and Edge HardnessSpecimens shall havean average hardness of not less than 15 lbf 67 N when testedin accordance with Method B:5.2.4 Nail Pull ResistanceSpecimens shall have an aver-age nail pull resistance of not less than the following whentested in accordance with Method B:Thickness,in.mmNail pull resistance,lbf N146.440 17871611.170 3141212.780 3565815.990 400