1、Designation:B67998(Reapproved 2015)Standard Specification forElectrodeposited Coatings of Palladium for EngineeringUse1This standard is issued under the fixed designation B679;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year
2、of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This specification covers requirements for electrodepos-ited palladium coatings containing at least 99.7 mass%ofpalladiu
3、m metal.Composite coatings consisting of palladiumwith a thin gold overplate for applications involving electricalcontacts are also covered.1.2 PropertiesPalladium is the lightest and least noble ofthe platinum group metals.It has a specific gravity of 12.0,which is substantially less than gold(19.3
4、)and platinum(21.5).This yields a greater volume or thickness of coatingand,consequently,some saving of metal weight accompaniedby a small sacrifice in corrosion resistance and reflectivity.Thefollowing table compares the hardness range of electrodepos-ited palladium with other electrodeposited nobl
5、e metals andalloys(1,2).2Approximate Hardness(HK25)Gold50250Palladium75600Platinum150550Palladium-Nickel300650Rhodium7501100Ruthenium60013001.3 The values stated in SI units are the preferred values.Values provided in parentheses are for information only.1.4 This standard does not purport to address
6、 all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2.Referenced Documents2.1 The following standards form a part o
7、f this specificationto the extent referenced herein:2.2 ASTM Standards:3B183 Practice for Preparation of Low-Carbon Steel forElectroplatingB242 Guide for Preparation of High-Carbon Steel for Elec-troplatingB254 Practice for Preparation of and Electroplating onStainless SteelB281 Practice for Prepara
8、tion of Copper and Copper-BaseAlloys for Electroplating and Conversion CoatingsB322 Guide for Cleaning Metals Prior to ElectroplatingB343 Practice for Preparation of Nickel for Electroplatingwith NickelB374 Terminology Relating to ElectroplatingB481 Practice for Preparation of Titanium and TitaniumA
9、lloys for ElectroplatingB482 Practice for Preparation of Tungsten and TungstenAlloys for ElectroplatingB487 Test Method for Measurement of Metal and OxideCoating Thickness by Microscopical Examination ofCross SectionB488 Specification for Electrodeposited Coatings of Goldfor Engineering UsesB489 Pra
10、ctice for Bend Test for Ductility of Electrodepos-ited and Autocatalytically Deposited Metal Coatings onMetalsB499 Test Method for Measurement of Coating Thicknessesby the Magnetic Method:Nonmagnetic Coatings onMagnetic Basis Metals1This specification is under the jurisdiction of ASTM Committee B08
11、onMetallic and Inorganic Coatings and is the direct responsibility of SubcommitteeB08.04 on Precious Metal Coatings.Current edition approved Nov.1,2015.Published December 2015.Originallyapproved in 1980.Last previous edition approved in 2009 as B679 98(2009).DOI:10.1520/B0679-98R15.2The boldface num
12、bers in parentheses refer to the list of references at the end ofthis specification.3For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page o
13、nthe ASTM website.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United States1 B507 Practice for Design of Articles to Be Electroplated onRacksB542 Terminology Relating to Electrical Contacts and TheirUseB558 Practice for Preparation of Nickel Alloys
14、for Electro-platingB567 Test Method for Measurement of Coating Thicknessby the Beta Backscatter MethodB568 Test Method for Measurement of Coating Thicknessby X-Ray SpectrometryB571 Practice for Qualitative Adhesion Testing of MetallicCoatingsB602 Test Method for Attribute Sampling of Metallic andIno
15、rganic CoatingsB689 Specification for Electroplated Engineering NickelCoatingsB697 Guide for Selection of Sampling Plans for Inspectionof Electrodeposited Metallic and Inorganic CoatingsB741 Test Method for Porosity In Gold Coatings On MetalSubstrates By Paper Electrography(Withdrawn 2005)4B748 Test
16、 Method for Measurement of Thickness of Metal-lic Coatings by Measurement of Cross Section with aScanning Electron MicroscopeB762 Test Method of Variables Sampling of Metallic andInorganic CoatingsB765 Guide for Selection of Porosity and Gross Defect Testsfor Electrodeposits and Related Metallic CoatingsB799 Test Method for Porosity in Gold and PalladiumCoatings by Sulfurous Acid/Sulfur-Dioxide VaporB809 Test Method for Porosity in Metallic Coatings byHumid Sulfur Vapor(“Flowers-of-Sulfur”)D1125