1、Designation:B68501(Reapproved 2012)Standard Specification forPalladium-Copper Electrical Contact Material1This standard is issued under the fixed designation B685;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of last revis
2、ion.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1.Scope1.1 This specification covers a 60%palladium-40%copperal
3、loy in the form of rod,wire,strip,and sheet material forelectrical contacts.1.2 The values stated in inch-pound units are to be regardedas standard.The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard.1.3 This s
4、tandard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to become familiarwith all hazards including those identified in the appropriateMaterial Safety Data Sheet(MSDS)for this product/materialas provided by th
5、e manufacturer,to establish appropriatesafety and health practices,and determine the applicability ofregulatory limitations prior to use.2.Referenced Documents2.1 ASTM Standards:2B476 Specification for General Requirements for WroughtPrecious Metal Electrical Contact Materials3.Manufacture3.1 Raw ma
6、terials shall be of such quality and purity thatthe finished product will have the properties and characteristicsprescribed in this specification.3.2 The material shall be finished by such operations(coldworking,annealing,turning,grinding,or pickling)as arerequired to produce the prescribed properti
7、es.4.Chemical Composition4.1 Material produced under the specification shall meet therequirements of chemical composition prescribed in Table 1.4.2 By agreement between purchaser and manufacturer,analysis may be required and limits established for elements orcompounds not specified in the table of c
8、hemical composition.5.Mechanical Requirements5.1 The contract or order may specify ultimate tensilestrength,elongation,microhardness(Knoop or Vickers),hard-ness(Rockwell or Rockwell Superficial),or a combination ofthese mechanical properties as temper criterion.If the contractor order does not speci
9、fy a temper criterion,then the criterionfor temper designation will be ultimate tensile strength andelongation(Table 2).5.2 Mechanical properties shall conform to the listings ofTable 3.5.3 All test specimens shall be full size when practical.5.4 All tests are to be conducted at room temperature,65
10、to85F(18 to 29C).6.General Requirements6.1 The provisions of Specifications B476 shall apply to allmaterials produced to this specification.7.Inspection and Testing7.1 Material furnished under this specification shall beinspected by the manufacturer as listed below:7.1.1 Visual inspection in accorda
11、nce with 11.2.1 in Speci-fication B476.7.1.2 Temper test(hardness or tension,but not both).Atension test is recommended for strip below 0.030 in.(0.8 mm)thickness and for wire of any diameter.A tension test ispreferred when permitted by part size and quantity.7.1.3 Dimensional tests.7.1.4 Spectrogra
12、phic or chemical analysis when indicatedby the purchase order.7.2 The purchaser shall perform such tests as are required toverify the quality of material procured under the specification.8.Keywords8.1 contact alloy;electrical contact alloy;palladium;palla-dium copper1This specification is under the
13、jurisdiction of ASTM Committee B02 onNonferrous Metals and Alloys and is the direct responsibility of SubcommitteeB02.05 on Precious Metals and Electrical Contact Materials.Current edition approved May 1,2012.Published May 2012.Originallyapproved in 1981.Last previous edition approved in 2006 as B68
14、5 01(2006).DOI:10.1520/B0685-01R12.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International,10
15、0 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United States1 APPENDIX(Nonmandatory Information)X1.TYPICAL PHYSICAL PROPERTIES OF 60 Pd-40 CuX1.1 The following is a list of typical property values whichare useful for engineering calculations in electrical contactdesign and applicati
16、on:Electrical resistivity,cm35(quenched)3.5(ordered)Density,g/cm3at 20C10.6Approximate liquidus,C1225Approximate solidus,C1195ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard.Users of this standard are expressly advised that determination of the validity of any such patent rights,and the riskof infringement of such rights,are entirely their own responsibility.This standard is subject to revision at an