1、Designation:A1089/A1089M14Standard Specification forHighly Loaded Anti-Friction Bearing Steel1This standard is issued under the fixed designation A1089/A1089M;the number immediately following the designation indicates theyear of original adoption or,in the case of revision,the year of last revision.
2、A number in parentheses indicates the year of lastreapproval.A superscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This specification covers bars,billets,and blooms ofbearing-quality steel to be used in the manufacture of highlyloaded anti-friction bea
3、rings.1.2 Supplementary requirements of an optional nature areprovided and when desired shall be so stated in the order.1.3 The values stated in either SI units or inch-pound unitsare to be regarded separately as standard.The values stated ineach system may not be exact equivalents;therefore,eachsys
4、tem shall be used independently of the other.Combiningvalues from the two systems may result in non-conformancewith the standard.2.Referenced Documents2.1 ASTM Standards:2A29/A29M Specification for General Requirements for SteelBars,Carbon and Alloy,Hot-WroughtA751 Test Methods,Practices,and Termino
5、logy for Chemi-cal Analysis of Steel ProductsE381 Method of Macroetch Testing Steel Bars,Billets,Blooms,and ForgingsE588 Practice for Detection of Large Inclusions in BearingQuality Steel by the Ultrasonic MethodE1019 Test Methods for Determination of Carbon,Sulfur,Nitrogen,and Oxygen in Steel,Iron,
6、Nickel,and CobaltAlloys by Various Combustion and Fusion TechniquesE2283 Practice for Extreme Value Analysis of NonmetallicInclusions in Steel and Other Microstructural Features2.2 Other Document:3ISO 4967 SteelDetermination of Content of NonmetallicInclusionsMicorgraphic Method Using Standard Dia-g
7、rams3.Ordering Information3.1 Orders for material under this specification shouldinclude the following information:3.1.1 Quantity,3.1.2 Grade identification,3.1.3 Specification designation and year of issue,3.1.4 Dimensions,and3.1.5 Supplementary requirements,if included.4.Process4.1 The steel shall
8、 be made by a basic oxygen or electricfurnace process,with vacuum degassing and suitableshrouding,that provides a high quality product meeting therequirements of this specification.The use of a vacuum-arcremelt or an electro-slag remelt process is not required but isnot excluded.5.Chemical Compositi
9、on and Analysis5.1 The chemical composition shall be agreed upon betweenthe manufacturer and purchaser.5.2 All compositions shall meet the element maximums ofTable 1.5.3 An analysis of each heat of steel shall be made by thesteel manufacturer in accordance with Test Methods,Practices,and Terminology
10、 A751.The chemical composition thus deter-mined shall conform to the requirements specified.5.4 Product analysis may be made by the purchaser inaccordance with Test Methods,Practices,and TerminologyA751.Permissible variations in product analysis shall be inaccordance with Specification A29/A29M.6.Si
11、zes,Shapes,and Dimensional Tolerances6.1 The physical size and shape of the material shall beagreed upon between manufacturer and purchaser.6.2 Dimensional tolerances shall conform to the require-ments specified in Specification A29/A29M.For sizes andshapes not covered by Specification A29/A29M,dime
12、nsionaltolerances shall be agreed upon between manufacturer andpurchaser.7.Quality Tests7.1 The supplier shall be held responsible for the quality ofthe material furnished and shall make the necessary tests to1This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Stee
13、l and Related Alloys and is the direct responsibility of SubcommitteeA01.28 on Bearing Steels.Current edition approved May 15,2014.Published July 2014.DOI:10.1520/A1089_A1089M-142For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For
14、Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.3Available from International Organization for Standardization(ISO),1,ch.dela Voie-Creuse,CP 56,CH-1211 Geneva 20,Switzerland,http:/www.iso.org.Copyright ASTM International,100 Barr Harbor
15、 Drive,PO Box C700,West Conshohocken,PA 19428-2959.United States1 ensure this quality.The supplier shall report results of themacroetch and micro-inclusion tests detailed below for eitherheat qualification or product qualification.7.2 SamplingSamples taken in accordance with the fol-lowing paragraph
16、s shall be obtained from rolled or forgedsections.A minimum 3 to 1 reduction of rolled or forgedsections is required for all products.7.3 Heat Qualification Sampling:7.3.1 For the qualification of an entire bottom poured heat,a minimum of six samples shall be examined and shallrepresent the top and bottom of three ingots.One ingot shall betaken at random from the first usable plate poured,one ingot atrandom from the usable plate poured nearest to the middle ofthe heat,and one ingot at random fro