1、Designation:A1053/A1053M121Standard Specification forWelded Ferritic-Martensitic Stainless Steel Pipe1This standard is issued under the fixed designation A1053/A1053M;the number immediately following the designation indicates theyear of original adoption or,in the case of revision,the year of last r
2、evision.A number in parentheses indicates the year of lastreapproval.A superscript epsilon()indicates an editorial change since the last revision or reapproval.1NOTEEditorially updated reference in 14.2 in April 2014.1.Scope*1.1 This specification covers seam welded ferritic-martensitic(dual phase)s
3、tainless steel pipe intended forabrasive and general corrosion service,manufactured with orwithout the addition of filler metal.Nominal sizes are NPS 2 toNPS 36 inclusive,with nominal(average)wall thickness up to0.75-in.(19 mm).1.2 The values stated in either inch-pound units or SI unitsare to be re
4、garded separately as standard.Within the text,theSI units are shown in brackets.The values stated in eachsystem may not be exact equivalents.Therefore,each systemshall be used independently of the other.Combining valuesfrom the two systems may result in non-conformance with thestandard.The inch-poun
5、d units shall apply unless the“M”designation is specified in the order.1.3 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the a
6、pplica-bility of regulatory limitations prior to use.2.Referenced Documents2.1 ASTM Standards:2A370 Test Methods and Definitions for Mechanical Testingof Steel ProductsA941 Terminology Relating to Steel,Stainless Steel,RelatedAlloys,and FerroalloysA999/A999M Specification for General Requirements fo
7、rAlloy and Stainless Steel PipeA1010/A1010M Specification for Higher-Strength Marten-sitic Stainless Steel Plate,Sheet,and StripA1016/A1016M Specification for General Requirements forFerritic Alloy Steel,Austenitic Alloy Steel,and StainlessSteel TubesE527 Practice for Numbering Metals and Alloys in
8、theUnified Numbering System(UNS)2.2 ANSI/ASME Standards:3B1.20.1 Pipe Threads,General PurposeB36.10 Welded and Seamless Wrought Steel PipeB36.19 Stainless Steel PipeASME Boiler and Pressure Vessel Code,Section IX42.3 Other Standard:SAE J1086 Practice for Numbering Metals and Alloys(UNS)53.Terminolog
9、y3.1 Definitions:3.1.1 The definitions in Specification A999/A999M andTerminology A941 are applicable to this specification.4.Ordering Information4.1 Orders for material to this specification shall conform tothe requirements of the current edition of Specification A999/A999M.5.General Requirements5.
10、1 Material furnished under this specification shall con-form to the applicable requirements of the current edition ofSpecification A999/A999M unless otherwise provided herein.6.Materials and Manufacture6.1 Material:6.1.1 The material for this pipe shall conform to Specifica-tion A1010/A1010M Grade 5
11、0 dual phase stainless steel.6.2 Manufacture:1This test method is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys and is the direct responsibility of SubcommitteeA01.10 on Stainless and Alloy Steel Tubular Products.Current edition approved Sept.1,2012.Publish
12、ed November 2012.Originallyapproved in 2006.Last previous edition approved in 2011 as A1053/A1053M11.DOI:10.1520/A1053_A1053M-12E01.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume informatio
13、n,refer to the standards Document Summary page onthe ASTM website.3Available from American National Standards Institute(ANSI),25 W.43rd St.,4th Floor,New York,NY 10036,http:/www.ansi.org.4Available from American Society of Mechanical Engineers(ASME),ASMEInternational Headquarters,Three Park Ave.,New
14、 York,NY 10016-5990,http:/www.asme.org.5Available from Society of Automotive Engineers(SAE),400 CommonwealthDr.,Warrendale,PA 15096-0001,http:/www.sae.org.*A Summary of Changes section appears at the end of this standardCopyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken
15、,PA 19428-2959.United States1Copyright by ASTM Intl(all rights reserved);6.2.1 The pipe shall be made using the following weldingmethods:Electric Resistance Welding(ERW)without theaddition of filler metal,submerged arc welding(SAW),or anautomatic fusion welding process with or without the additionof
16、 filler metal during the welding process.6.2.2 The welded joints made with the addition of fillermetal shall be made with procedures and by welders or weldingoperators that are qualified in accordance with the ASMEBoiler and Pressure Vessel Code,Section IX.6.2.3 Welded pipe of NPS 14 and smaller shall have a singlelongitudinal weld.Welded pipe of a size larger than NPS 14shall have a single longitudinal weld or shall be produced byforming and welding two longitudinal sections of flat stockwhen a