1、Designation:D60917(Reapproved 2022)Standard Practice forPreparation of Cold-Rolled Steel Panels for Testing Paint,Varnish,Conversion Coatings,and Related CoatingProducts1This standard is issued under the fixed designation D609;the number immediately following the designation indicates the year ofori
2、ginal adoption or,in the case of revision,the year of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S.Department of Def
3、ense.1.Scope1.1 This practice covers various types of cold rolled steelpanels and the procedures to be followed in their preparationfor testing paint,varnish,lacquer,conversion coatings,andrelated products.1.2 The procedures are as follows:Procedure AConversion coatings(phosphates,chromates,etc.)Pro
4、cedure BVapor degreasingProcedure CSolvent brushingProcedure DSolvent wipingProcedure EAlkaline cleaning1.3 The values stated in SI units are to be regarded as thestandard.The values given in parentheses are for informationonly.1.4 This standard does not purport to address all of thesafety concerns,
5、if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practices and deter-mine the applicability of regulatory limitations prior to use.1.5 This international standard was developed in accor-dance with internatio
6、nally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2A109/A109M Spe
7、cification for Steel,Strip,Carbon(0.25Maximum Percent),Cold-RolledA1008/A1008M Specification for Steel,Sheet,Cold-Rolled,Carbon,Structural,High-Strength Low-Alloy,High-Strength Low-Alloy with Improved Formability,RequiredHardness,Solution Hardened,and Bake HardenableD235 Specification for Mineral Sp
8、irits(Petroleum Spirits)(Hydrocarbon Dry Cleaning Solvent)3.Summary of Practice3.1 Several procedures are described for the preparation andcleaning of the steel test panels shown in Table 1.4.Significance and Use4.1 The procedures described in this practice are designed toprovide steel panels with a
9、 uniform and reproducible surfacefor testing of paint,varnish,lacquer,conversion coatings,andrelated products.5.Test Panels5.1 Prepare the test panels from rust and stain-free cold-rolled steel as described in 5.2,5.3,5.4,and Table 1.Thepanels shall be made to a size and thickness as agreed uponbetw
10、een the purchaser and seller.Edges shall be smooth andcorners rounded.The steel may have been coated at the millwith a suitable rust preventive compound for protection duringshipment and storage.However,long-term steel storage withoil on the surface may cause an oil/steel reaction known as oilstain.
11、Since such stains inhibit chemical bonding,the steelselected for panels shall be free of oil stain and other visibleprocessing variation caused by pickling or annealing.5.2 Type 1 steel has a matte finish produced by steel millrolls that have been grit blasted.This finish is typical ofcold-rolled st
12、eel used for painted surfaces on automobiles,appliances,etc.Such surfaces can be partially characterized bymeasuring the average peak-to-valley distance and the numberof peaks per unit area.However,conversion coating and paintperformance on such surfaces may vary because of differentoxidation,anneal
13、ing procedures,and surface conditions.1This practice is under the jurisdiction of ASTM Committee D01 on Paint andRelated Coatings,Materials,and Applications and is the direct responsibility ofSubcommittee D01.27 on Accelerated Testing.Current edition approved June 1,2022.Published June 2022.Original
14、lyapproved in 1941.Last previous edition approved in 2017 as D609 17.DOI:10.1520/D0609-17R22.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summa
15、ry page onthe ASTM website.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for t
16、heDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.15.3 Type 2 steel panels are flat polished(or“ground”)afterthe steel has been received from the mill.Flat polishing is amethod of mechanically grinding the surface with abrasivebelts to remove surface contaminants and provide a moreuniform and reproducible surface for testing.Flat-polishedpanels are not representative of the surface on which mostcoa