1、Designation:D470413(Reapproved 2017)Standard Test Method forTearing Strength,Tongue Tear of Leather1This standard is issued under the fixed designation D4704;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of last revision.A
2、 number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S.Department of Defense.1.Scope1.1 This test method is intended for determining the tear
3、ingstrength of leather by measuring the force required to tear aspecimen cut perpendicular to the surface.This test methoddoes not apply to wet blue.1.2 The values stated in inch-pound units are to be regardedas standard.The values given in parentheses are mathematicalconversions to SI units that ar
4、e provided for information onlyand are not considered standard.1.3 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practices and deter-min
5、e the applicability of regulatory limitations prior to use.1.4 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations i
6、ssued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2D1610 Practice for Conditioning Leather and Leather Prod-ucts for TestingD1813 Test Method for Measuring Thickness of LeatherTest SpecimensD2209 Test Method for Tensile Strength o
7、f LeatherD2813 Practice for Sampling Leather for Physical andChemical Tests3.Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 tongue tear strengththe load required to tear theleather between two tongues formed by splitting the leatherperpendicular to its surface.4.Significance and
8、 Use4.1 Knowledge of the strength of the sample can be adetermining factor for the end use of the product.5.Apparatus5.1 Testing Machine,as described in Test Method D2209.5.2 Thickness Gage,a dead weight type of thickness gage asdescribed in Test Method D1813.5.3 Steel Die,to cut test specimens.6.Sa
9、mpling and Test Specimens6.1 Unless otherwise specified,sample the leather accordingto Practice D2813.6.2 The specimen shall be a rectangular piece of leather,1 4 in.(25.4 101.6 mm)by the full thickness of the unit.Itshall have a316in.(4.76 mm)hole located on the long axis 1in.(25.4 mm)from one end
10、and shall be split along its axisfrom the hole to the other end to form two tongues.Thedirection of the long axis of the specimen relative to thebackbone shall be noted.See Fig.1.7.Conditioning7.1 All specimens shall be conditioned and tested in anatmosphere as described in Practice D1610.8.Procedur
11、e8.1 Determine the thickness of the specimen to the nearest0.001 in.(0.01 mm)on the long axis between the hole and theunsplit end of the specimen.The gage foot shall be adjacent to,but shall not overlap,the hole.8.2 Clamp one of the tongues on the specimen in each of thetesting grips so that the lon
12、g axis of the tongue is in thedirection of the motion of the movable grip.The faces of thegrips shall be approximately 2 in.(50.8 mm)from the commonbase of the tongues(from the hole).1This test method is under the jurisdiction of ASTM Committee D31 on Leatherand is the direct responsibility of Subco
13、mmittee D31.07 on Physical PropertiesCurrent edition approved Sept.1,2017.Published October 2017.Originallyapproved in 1987.Last previous edition approved in 2013 as D4704 13.DOI:10.1520/D4704-13R17.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at
14、 serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance wit
15、h internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.1 8.3 Operate the machine at 10 6 2 in.(254 6
16、 50.8 mm)perminute until the specimen starts to tear.At the instant of theinitial tear,note and record the load registered by the machine.9.Report9.1 The thickness measurement of all specimens tested shallbe averaged to the nearest 0.001 in.(0.01 mm)and reported asthe thickness of the sample.9.2 The load required to tear the specimens shall be aver-aged to the nearest pound and reported as the tongue tearstrength of the sample.9.3 The direction of the long axis of the specimen relative tothe bac