1、Designation:D319006(Reapproved 2021)Standard Test Method forRubberEvaluation of Chloroprene Rubber(CR)1This standard is issued under the fixed designation D3190;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of last revisio
2、n.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This test method covers the standard materials,testformulas,mixing procedures and test methods for evaluationand quality control testin
3、g of chloroprene rubbers(CR).CRcan be generally classified according to the two types ofpolymerization modifiers used in their manufacture:sulfurmodified types and mercaptan modified types.1.2 The values stated in SI-units are to be regarded as thestandard.The values in parentheses are for informati
4、on only.1.3 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practices and deter-mine the applicability of regulatory limitations prior to
5、use.1.4 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers
6、 to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2D412 Test Methods for Vulcanized Rubber and Thermoplas-tic ElastomersTensionD1646 TestMethodsforRubberViscosity,StressRelaxation,andPre-VulcanizationCharacteristics(Mooney Viscometer)D2084 Test Method for Rubber PropertyVulcanizationU
7、sing Oscillating Disk Cure MeterD3182 Practice for RubberMaterials,Equipment,and Pro-cedures for Mixing Standard Compounds and PreparingStandard Vulcanized SheetsD3896 Practice for Rubber From Synthetic SourcesSamplingD4483 Practice for Evaluating Precision for Test MethodStandards in the Rubber and
8、 Carbon Black ManufacturingIndustriesD5289 Test Method for Rubber PropertyVulcanizationUsing Rotorless Cure MetersD6204 Test Method for RubberMeasurement of Unvulca-nized Rheological Properties Using Rotorless Shear Rhe-ometers3.Summary of Test Method3.1 Separatestandardgumorcarbonblackfilledformula
9、tions,or both,using different samples of CR,areprepared on a laboratory mill or in a Miniature Internal Mixer(MIM)in accordance with Practice D3182.3.2 See Test Method D1646 for Mooney scorch times andTest Method D2084 or D5289 for cure meter data of theformulations.3.3 Tensile sheets for stress/str
10、ain testing are vulcanized inaccordance with Practice D3182 and 100 and 300%modulus,tensile strength and elongation at break are measured inaccordance with Test Method D412.4.Significance and Use4.1 This test method is intended for referee purposes,butmay be used for quality control,research and dev
11、elopmenttesting and comparison of different rubber samples in astandard formula.4.2 This test method may also be used to obtain values forcustomer acceptance of rubber.4.3 This test method is a revision of Test Methods D3190(prior to 1991),with 3-methyl thiazolidine thione-2 beingsubstituted for eth
12、ylene thiourea(ETU),a suspected carcino-gen.5.Standard Test Formulae5.1 The Standard Test Formulae are shown in Table 1.Formulae Nos.1 and 2 shall be used for sulfur modified CRand Nos.3 and 4 for mercaptan modified CR.6.Sample Preparation6.1 Obtain and prepare the test samples in accordance withPra
13、ctice D3896.1This test method is under the jurisdiction of ASTM Committee D11 on Rubberand Rubber-like Materials and is the direct responsibility of Subcommittee D11.23on Synthetic Rubbers.Current edition approved Nov.1,2021.Published December 2021.Originallyapproved in 1973.Last previous edition ap
14、proved in 2016 as D3190 06(2016).DOI:10.1520/D3190-06R21.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.Copyright
15、 ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Stand
16、ards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.1?7.Mixing Procedure7.1 The following three mixing procedures are offered:7.1.1 Mill Method AFor Formulae Nos.1 and 2.7.1.2 Mill Method BFor Formulae Nos.3 and 4.7.1.3 Miniature Internal Mixer MethodFor Formulae Nos.1,2,3 and 4.7.1.4 Laboratory BanburyAll FormulaeNOTE1It is not implied that comparable results will be obtained bythese methods.NOTE2The indicated mill openings are desire