1、Designation:D348406(Reapproved 2022)Standard Test Methods forRubberEvaluation of Oil-Extended Solution BR(Polybutadiene Rubber)1This standard is issued under the fixed designation D3484;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision
2、,the year of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 These test methods cover the standard materials,testformulas,mixing procedures,and test methods for the evalu-
3、ation and production control of oil-extended polybutadienerubber(OE-BR)polymerized in an appropriate solution.1.2 The values stated in SI units are to be regarded as thestandard.The values given in parentheses are for informationonly.1.3 This standard does not purport to address all of thesafety con
4、cerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practices and deter-mine the applicability of regulatory limitations prior to use.1.4 This international standard was developed in accor-dance with inte
5、rnationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2D412 Tes
6、t Methods for Vulcanized Rubber and Thermoplas-tic ElastomersTensionD1646 TestMethodsforRubberViscosity,StressRelaxation,andPre-VulcanizationCharacteristics(Mooney Viscometer)D2084 Test Method for Rubber PropertyVulcanizationUsing Oscillating Disk Cure MeterD3182 Practice for RubberMaterials,Equipme
7、nt,and Pro-cedures for Mixing Standard Compounds and PreparingStandard Vulcanized SheetsD3896 Practice for Rubber From Synthetic SourcesSamplingD4483 Practice for Evaluating Precision for Test MethodStandards in the Rubber and Carbon Black ManufacturingIndustriesD5289 Test Method for Rubber Property
8、VulcanizationUsing Rotorless Cure MetersD6204 Test Method for RubberMeasurement of Unvulca-nized Rheological Properties Using Rotorless Shear Rhe-ometers2.2 ISO Standard:ISO 2476 Rubber,Butadiene(BR)Solution PolymerizedTypesTest Recipe and Evaluation Characteristics33.Significance and Use3.1 These t
9、ests are mainly intended for referee purposes butmay also be used for quality control of rubber production.Theymay be used in research and development work for comparisonof different rubber samples in a standard formula.3.2 These test methods may also be used to obtain values forcustomer acceptance
10、of rubber.4.Standard Test Formulas4.1 Standard FormulasSee Table 1.4.2 Formula 1 is written based on 100 parts of rubber whileFormula 2 is written on the basis of 100 parts of themasterbatch.Either formula may be used,but these will notgive the same results.NOTE1Formula 2 is specified in ISO 2476 fo
11、r oil extended BR.5.Sample Preparation5.1 For test intended for referee purposes obtain and preparethe test samples in accordance with Practice D3896.6.Mixing Procedures6.1 The following four mixing test methods are offered:6.1.1 Method AInternal Mixer Procedure(6.2),6.1.2 Method BInternal Mixer/Mil
12、l Procedure(6.3),1These test methods are under the jurisdiction of ASTM Committee D11 onRubber and Rubber-like Materials and are the direct responsibility of SubcommitteeD11.23 on Synthetic Rubbers.Current edition approved Oct.1,2022.Published October 2022.Originallyapproved in 1976.Last previous ed
13、ition approved in 2016 as D3484 06(2016).DOI:10.1520/D3484-06R22.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.3
14、Available from American National Standards Institute,25 W.43rd St.,4thFloor,New York,NY 10036.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles
15、 on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.16.1.3 Method CMill Procedure(6.4),and6.1.4 Method DMiniature Internal Mixer Procedu
16、re(6.5).NOTE2It is not implied that comparable results will be obtained bythese test methods.NOTE3Since the mill handling characteristics of the solution polyb-utadiene rubbers are somewhat more difficult than that of other rubbers theuse of one of the internal mixer procedures is recommended(Method A,B,or D).The mill procedure(Method C)may be used provided a goodcarbon black dispersion is obtained.6.2 Internal Mixer Initial Mix(Methods A,B):6.2.1 For general mixing procedure refer to Practice D