1、Designation:D220816Standard Test Method forBreaking Strength of Leather by the Grab Method1This standard is issued under the fixed designation D2208;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of last revision.A number i
2、n parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S.Department of Defense.1.Scope1.1 This test method covers the determination of the break-ing str
3、ength of leather by the grab method.It is intended for useon light,soft leathers;boarded,sueded,or embossed leatherstested on a specimen in the form of a rectangle piece;narrowstrap,welt,lace,and round belt leathers;or other leathers thatcannot be accurately tested by Test Method D2209.This testmeth
4、od does not apply to wet blue.1.2 The test method is not recommended for breaking loadsover 500 lbf(2200 N)because of slippage of the specimen inthe jaws.1.3 The values stated in inch-pound units are to be regardedas the standard.The values given in parentheses are forinformation only.1.4 This stand
5、ard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2.Referenced Documents2.1 ASTM S
6、tandards:2D1517 Terminology Relating to LeatherD1610 Practice for Conditioning Leather and Leather Prod-ucts for TestingD1813 Test Method for Measuring Thickness of LeatherTest SpecimensD2209 Test Method for Tensile Strength of LeatherD2211 Test Method for Elongation of Leather3.Terminology3.1 For d
7、efinitions of leather terms used in this standard,refer to Terminology D1517.4.Summary of Test Method4.1 The leather specimen is clamped in the test machine asdescribed in Test Method D2209.The force required to rupturethe leather at a jaw separation of 10 6 2 in./min is measured,along with the perc
8、ent elongation at rupture.5.Significance and Use5.1 The measurement of the strength of leather is oftennecessary in order to determine its suitability for its intendedapplication.This test method is recommended for use on light,soft leathers,narrow strap,welt,lace and round belt leathers aswell as o
9、thers that cannot be accurately tested by Test MethodD2209.6.Apparatus6.1 Testing Machine,as described in Test Method D2209.NOTE1The face of one jaw of each clamp shall measure 1 by 1 in.(25.4 by 25.4 mm)and that of the other shall measure 1 by 112(25.4 by38 mm)or more for testing specimens wider th
10、an the jaws only.6.2 Thickness GageAdead-mass type of thickness gage asdescribed in Test Method D1813.6.3 Steel Scale,graduated to read in 0.02 in.(0.5 mm).7.Sampling,Test Specimens,and Test Units7.1 For testing specimens wider than the jaws,the specimenfor wide,flat leathers shall be a small piece
11、of leather 6 in.(152mm)long and 3 in.(76 mm)wide.The direction of the longdimension relative to the backbone shall be noted.7.2 For testing specimens cut from narrow strip,the speci-men for narrow strap,welting,lace,and round belt leathersshall be a piece of leather 6 in.(152 mm)long.8.Conditioning8
12、.1 Conditions as described in Practice D1610.9.Procedure9.1 For Testing Specimens Wider than the Jaws:1This test method is under the jurisdiction of ASTM Committee D31 on Leatherand is the direct responsibility of D31.05 on Upholstery.This test method wasdeveloped in cooperation with the American Le
13、ather Chemists Assn.(StandardsMethod E161965).Current edition approved Sept.1,2016.Published October 2016.Originallyapproved in 1963.Last previous edition approved in 2010 as D220800(2016).DOI:10.1520/D2208-16.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer
14、 Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United States1 9.1.1 Measure the thickness of the specimen to
15、 the nearest0.001 in.(0.025 mm)in three places:at the center and on thelong axis 1 in.(25.4 mm)each side of the center.9.1.2 The distance between the grips at the start of the testshall be 3 618in.(76 6 3.2 mm).9.1.3 The face of one jaw of each clamp shall measure 1 by1 in.(25.4 by 25.4 mm).9.1.4 Pl
16、ace the specimen in the testing machine with its longaxis parallel to the direction of the applied force,and clamplightly.Distribute the material of the specimen uniformly andhang flat between the jaws before tightly clamping the speci-men.9.1.5 Determine the elongation of the specimen in accor-dance with Test Method D2211.9.1.6 Operate the machine so that the movable clamp travelsat a uniform speed of 10 6 2 in./min(254 6 50 mm/min)whenrunning free.9.1.7 Record the load required to rupture the