1、Designation:D220700(Reapproved 2021)Standard Test Method forBursting Strength of Leather by the Ball Method1This standard is issued under the fixed designation D2207;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of last re
2、vision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S.Department of Defense.1.Scope1.1 This test method covers the determination of
3、the burst-ing strength of leather by the ball method.It may be used to testa large variety of leathers and leather products.It is particularlyapplicable to light-and medium-weight leathers,such as shoeuppers and garments.This test method does not apply to wetblue.1.2 The values stated in inch-pound
4、units are to be regardedas standard.The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard.1.3 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibi
5、lity of the user of this standard to establish appro-priate safety,health,and environmental practices and deter-mine the applicability of regulatory limitations prior to use.1.4 This international standard was developed in accor-dance with internationally recognized principles on standard-ization es
6、tablished in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2D1517 Terminology Relating to LeatherD1610 Practice for Conditio
7、ning Leather and Leather Prod-ucts for TestingD1813 Test Method for Measuring Thickness of LeatherTest SpecimensD2209 Test Method for Tensile Strength of Leather3.Terminology3.1 For definitions of leather terms used in this standardrefer to Terminology D1517.4.Summary of Test Method4.1 The leather s
8、pecimen is mounted in the ball burst fixturewhich is attached to a testing machine,as described in TestMethod D2209.The machine is operated at a jaw separation of4 6 1 in./min.The maximum load registered is recorded.Thebursting strength in lb/in.of thickness is calculated by dividingthe bursting loa
9、d by the thickness of the specimen.5.Significance and Use5.1 This test method is designed to measure the burstingstrength of leather by measuring the force required to force aspherical ended plunger through a piece of leather.Thebursting load and extension will be generally proportional tothe diamet
10、er of the plunger.This test method is suitable fordevelopment,control and service evaluation of the leather.There is good correlation between bursting strength and tensilestrength.This test method may not apply when the conditionsof the test employed differ widely from those specified in thetest met
11、hod.6.Apparatus6.1 Testing Machine,as described in Test Method D2209.NOTE1The machine shall have a cross-head speed of 4 6 1 in./min(1.6 6 0.4 mm/s).6.2 Thickness GaugeAdead-mass type of thickness gaugeas described in Test Method D1813.6.3 Burst Tester,3as shown in Fig.1.The diameter of theball or p
12、lunger shall be14in.(0.250 in.(6.4 mm).6.4 Parts Required to Modify Burst Tester,as illustrated inFig.2,or equivalent.6.5 Die,Knife,or Shears,for cutting the test specimen.1This test method is under the jurisdiction of ASTM Committee D31 on Leatherand is the direct responsibility of Subcommittee D31
13、.07 onPhysical Properties Thistest method was developed in cooperation with the American Leather ChemistsAssn.(Standard Method E14 1965).Current edition approved Sept.1,2021.Published October 2021.Originallyapproved in 1964.Last previous edition approved in 2015 as D2207 00(2015).DOI:10.1520/D2207-0
14、0R21.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.3A modified Scott Model W Burst Tester has been found satisfa
15、ctory for thispurpose.Available from Precision Scientific,3737 W.Cortland,Chicago,IL 60647.Request Ball Burst Fixture Catalog,No.26651.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance w
16、ith internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.16.6 Dial Gauge,mounted on the burst tester as shown inFig.1 to measure the height of the extension of the leatherspecimen.NOTE2This gauge shall be calibrated to read directly to the nearest0.001 in.(0.025 mm).It shall be equipped with a flat