1、Designation:A85304(Reapproved 2017)Standard Specification forSteel Wire,Carbon,for General Use1This standard is issued under the fixed designation A853;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of last revision.A numbe
2、r in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S.Department of Defense.1.Scope1.1 This specification covers carbon steel wire,supplied incoil
3、s,for general use.It may be produced hard drawn,annealedin process,or annealed at finish size.1.2 The values stated in inch-pound units are to be regardedas standard.No other units of measurement are included in thisstandard.2.Referenced Documents2.1 ASTM Standards:2A370 Test Methods and Definitions
4、 for Mechanical Testingof Steel ProductsA510 Specification for General Requirements for Wire Rodsand Coarse Round Wire,Carbon SteelA700 Guide for Packaging,Marking,and Loading Methodsfor Steel Products for ShipmentA751 Test Methods,Practices,and Terminology for Chemi-cal Analysis of Steel ProductsE2
5、9 Practice for Using Significant Digits in Test Data toDetermine Conformance with Specifications2.2 Military Standards:3MIL-STD-129 Marking for Shipment and StorageMIL-STD-163 Steel Mill Products,Preparation for Ship-ment and Storage2.3 Federal Standard:Fed.Std.No.123 Marking for Shipments(Civil Age
6、ncies)32.4 AIAG Standard:AIAGB-5 02.00 Primary Metals Identification Tag Applica-tion Standard43.Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 annealed-in-process wiresteel wire that was ther-mally treated and subsequently redrawn.3.1.2 annealed wirewire that was drawn to size
7、andannealed at finish size.3.1.3 carbon steelsteel is considered to be carbon steelwhen no minimum content is specified or required foraluminum,chromium,cobalt,columbium,molybdenum,nickel,titanium,tungsten,vanadium,or zirconium or any otherelement added to obtain a desired alloying effect;when thesp
8、ecified minimum copper content does not exceed 0.40%;orwhen the maximum content for any of the following elementsdoes not exceed these percentages:manganese 1.65,silicon0.60,or copper 0.60(see Specification A510).3.1.4 hard drawn wirewire drawn without the use ofthermal treatment.4.Ordering Informat
9、ion4.1 It shall be the responsibility of the purchaser to specifyall requirements that are necessary for material under thisspecification.Such requirements include,but are not limited to,the following:4.1.1 Quantity(weight in pounds),4.1.2 Name of material(carbon steel wire),4.1.3 Wire diameter in i
10、nches,to the third decimal point,4.1.4 Chemical composition grade number,4.1.5 Condition(hard drawn,annealed in process,annealedat finished size),4.1.6 Finish(see Section 10),4.1.7 Packaging,and4.1.8 ASTM designation and year of issue.NOTE1A typical ordering description is as follows:40 000 lb,0.148
11、in.,Bright Hard Drawn Carbon Steel Wire,Grade 1008,in 600-lb.1This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys and is the direct responsibility of SubcommitteeA01.03 on Steel Rod and Wire.Current edition approved March 15,2017.Published M
12、arch 2017.Originallyapproved in 1985.Last previous edition approved in 2010 as A853 04(2010).DOI:10.1520/A0853-04R17.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the
13、standards Document Summary page onthe ASTM website.3Available from Standardization Documents Order Desk,DODSSP,Bldg.4,SectionD,700RobbinsAve.,Philadelphia,PA19111-5098,http:/dodssp.daps.dla.mil.4Available from Automotive Industry Action Group(AIAG),26200 Lahser Rd.,Suite 200,Southfield,MI 48033,http
14、:/www.aiag.org.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopmen
15、t of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.1 catch-weight coils on tubular carriers to ASTM ACSW.5.Materials and Manufacture5.1 The steel shall be made by any commercially acceptedsteel making process.The s
16、teel may be either ingot cast orstrand cast.6.Chemical Composition6.1 The grade designation shall be as specified in thepurchase order.6.2 Chemical ranges and limits,and procedures for analysisshall be in accordance with Test Methods,Practices,andTerminology A751.7.Mechanical Properties7.1 The carbon steel wire shall meet the tensile strengthrequirements shown in Table 1 for the condition specified whentested in accordance with Test Methods and Definitions A370.8.Dimensions and Tolerances8.1 The