1、Designation:D482413(Reapproved 2018)Standard Test Method forDetermination of Catalyst Acidity by AmmoniaChemisorption1This standard is issued under the fixed designation D4824;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year
2、of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.INTRODUCTIONThis test method involves the measurement of total catalyst acidity by chemisorption of ammoniain a static volumetric s
3、ystem.Acidity is a very important property in determining catalyst activity andselectivity in many commercial reactions.Zeolite based catalysts used in the petroleum industry forcatalytic cracking are a prime example.This test method describes a simple procedure employinginexpensive equipment that c
4、ould readily be assembled in most laboratories.1.Scope1.1 This test method covers the determination of acidity ofcatalysts and catalyst carriers by ammonia chemisorption.Avolumetric measuring system is used to obtain the amount ofchemisorbed ammonia.1.2 The values stated in SI units are to be regard
5、ed asstandard.The values given in parentheses after SI units areprovided for information only and are not considered standard.1.3 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro
6、-priate safety,health,and environmental practices and deter-mine the applicability of regulatory limitations prior to use.1.4 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevel
7、opment of International Standards,Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2D3766 Terminology Relating to Catalysts and CatalysisE691 Practice for Conducting an Interlaboratory Study toDetermi
8、ne the Precision of a Test Method3.Terminology3.1 DefinitionsSee Terminology D3766.3.2 Symbols:Vk=calibrated expansion volume,cm3.T1=temperature of Vkat initial ammonia pressure,K.T2=temperature of Vkat final ammonia pressure,K.P1=initial ammonia pressure,torr.P2=final ammonia pressure,torr.Ws=mass
9、of sample,g.W1=tare of sample tube,g.W2=sample mass plus tare of tube,g.P1T=initial ammonia pressure corrected to standardtemperature,torr.P2T=final ammonia pressure corrected to standardtemperature,torr.4.Summary of Test Method4.1 A sample is degassed by heating in a vacuum to removeadsorbed vapors
10、 from the surface.The sample is then exposedto an excess of gaseous ammonia and the excess ammonia isremoved by freezing it into a trap cooled with liquid nitrogen.The chemisorbed ammonia is calculated as the differencebetween the volume of ammonia before exposure and thevolume recovered in the liqu
11、id nitrogen trap.5.Significance and Use5.1 This test method can be used to determine the acidity ofcatalysts and catalyst carriers by ammonia chemisorption formaterials specifications,manufacturing control,and researchand development in the evaluation of catalysts.1This test method is under the juri
12、sdiction of ASTM Committee D32 onCatalysts and is the direct responsibility of Subcommittee D32.01 on Physical-Chemical Properties.Current edition approved Nov.1,2018.Published December 2018.Originallyapproved in 1988.Last previous edition approved in 2013 as D4824 13.DOI:10.1520/D4824-13R18.2For re
13、ferenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Consh
14、ohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organi
15、zation Technical Barriers to Trade(TBT)Committee.1 6.Apparatus6.1 A schematic diagram of one type of apparatus is shownin Fig.1.It may be constructed of glass or metal and mayoperate manually or automatically.It has the following fea-tures:6.1.1 Vacuum System,capable of attaining and maintainingpres
16、sures below 104torr(0.01 Pa)in the absence of catalyst.6.1.2 Expansion Vessel,having a volume between 300 to500 cm3(Vk)known to the nearest 0.01 cm3(Note 1).Thisvolume is defined as the volume between stopcocks V7and V8and includes the pressure gage and ammonia bulb.NOTE1An expansion vessel of smaller volume is recommended formaterials of low surface area or smaller sample size.6.1.3 Pressure Sensing Device or Pressure Transducer,capable of measuring 0 to 250 torr to the nearest 101torr(10Pa).6.