1、Designation:D283589(Reapproved 2017)Standard Specification forLubricant for Installation of Preformed Compression Sealsin Concrete Pavements1This standard is issued under the fixed designation D2835;the number immediately following the designation indicates the year oforiginal adoption or,in the cas
2、e of revision,the year of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S.Department of Defense.1.Scope*1.1 This specif
3、ication covers a lubricant suitable for facili-tating the insertion and positioning of preformed elastomericcompression seals in prepared voids(usually contractionjoints)in concrete pavement.1.2 The requirements of the lubricant are based on theperformance of the lubricant as measured by its solids
4、content,homogeneity,consistency,and drying rate.1.3 The values stated in inch-pound units are to be regardedas the standard.The metric equivalents of U.S.customary unitsmay be approximate.1.4 The following precautionary caveat pertains only to thetest method portion,Section 7 of this specification.T
5、hisstandard does not purport to address all of the safety concerns,if any,associated with its use.It is the responsibility of the userof this standard to establish appropriate safety and healthpractices and determine the applicability of regulatory limita-tions prior to use.1.5 This international st
6、andard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Ref
7、erenced Documents2.1 ASTM Standards:2D1084 Test Methods for Viscosity of AdhesivesD1644 Test Methods for Nonvolatile Content of Varnishes3.Classification3.1 The lubricant shall be based on polychloroprene,con-taining only soluble phenolic resins blended together withantioxidants and acid acceptors i
8、n a suitable mixture of organicsolvents.4.Requirements4.1 HomogeneityThe lubricant shall be uniform and con-tain no lumps or agglomerates.4.2 Solids ContentThe nonvolatile content of the lubricantshall be no less than 24.0 weight%.4.3 ConsistencyThe lubricant shall exhibit a viscosity inone of the f
9、ollowing ranges:4.3.1 Type IFor hand or machine application,3000 to8000 cP.4.3.2 Type IIFor machine application,8000 to 15 000 cP.4.4 Drying RateA bond between lubricant-coated papersprepared after 8-min drying time shall separate completely inless than 10 s when a 50-g load is applied in shear.A si
10、milarbond prepared after 20-min drying time shall remain un-separated for a minimum of 10 s when a 50-g load is appliedin shear.5.Basis of Purchase5.1 Each lot of lubricant shall be accompanied by themanufacturers certified test results attesting compliance withthis specification,unless an alternati
11、ve agreement is concludedby the manufacturer and the purchaser.6.Sampling6.1 The lubricant samples shall be a 1-quart(1-litre)aliquotconsisting of a composite taken when possible from three ormore separate containers chosen at random.Samples also shallbe taken from containers which appear to be nonr
12、epresentativeand shall be tested separately.Before a sample is withdrawn,the contents in the container shall be mixed to uniformconsistency.The sample shall be placed immediately in anairtight glass jar or metal can until tested.1This specification is under the jurisdiction of ASTM Committee D04 on
13、Roadand Paving Materials and is the direct responsibility of Subcommittee D04.34 onPreformed Joint Fillers,Sealers and Sealing Systems.Current edition approved July 1,2017.Published July 2017.Originally approvedin 1969.Last previous edition approved in 2012 as D2835 89(2012).DOI:10.1520/D2835-89R17.
14、2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.*A Summary of Changes section appears at the end of this standardC
15、opyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of Internation
16、al Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.1 7.Test Methods7.1 HomogeneityStir the test sample by hand for 2 minwith a spatula.Withdraw the spatula and examine the lubricantas it flows from the spatula for lumps or agglomerates.Particles smaller in diameter than 0.015 in.(0.38 mm)shall notbe considered cause for rejection.NOTE1At the consumers request,compliance with the 0.015-in.(0.38-mm)requirement shall be determine